Effects of ball milling time on the microstructure and hydrogen storage performances of Ti21.7Y0.3Fe16Mn3Cr alloy
Zeming Yuan,Yongqi Sui,Qian Yuan,Zhen Qi,Tingting Zhai,Xiaoming Li,Tao Li
DOI: https://doi.org/10.1016/j.ijhydene.2022.09.027
IF: 7.2
2023-04-01
International Journal of Hydrogen Energy
Abstract:TiFe alloy can store hydrogen at room temperature and low hydrogen pressure, and its theoretical hydrogen storage capacity is up to 1.8 wt%. However, TiFe alloy needs to be activated at high pressure (5 MPa hydrogen) and high temperature (673–723 K), which limits the practical application of TiFe alloy. The as-cast Ti21.7Y0.3Fe16Mn3Cr alloy was milled for 0, 0.5, 0.75, 1, and 3 h to study the effects of ball milling on phase structures and hydrogen storage performances. Emphasis was focused on the activation process of as-milled alloys at different temperatures, including the activation process at 483, 443, and 403 K. The results show that the alloys were consisted of TiFe phase, and [Fe, Cr] solid solution. The nanocrystalline boundary produced by milling and the phase boundary provided by the second phase provide a large number of channels for hydrogen diffusion and promote the improvement of hydrogen storage performances. The time required for activation process of as-milled alloys was significantly reduced, and the activation time of as-milled (0.75 h) was only 4 min, and its enthalpy variation for hydrogen absorption and desorption was 22.943 and 26.215 kJ mol−1 H2, respectively.
energy & fuels,electrochemistry,chemistry, physical