Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

HANG Zhou-min,XIAO Xue-zhang,WU Zhe,LI Shou-quan,GE Hong-wei,CHEN Chang-pin,CHEN Li-xin

DOI: https://doi.org/10.3321/j.issn:1001-9731.2009.11.023

2009-01-01

Abstract:Ti10V83-xFe6ZrMnx(x=0,2,4,6) hydrogen storage alloys were prepared by induction melting with magnetic levitation,and the effects of Mn content on the microstructures and hydrogen storage properties of the alloys have been investigated systematically. XRD and SEM analyses show that the Mn-free alloy with x=0 has a single Ti-V based solid solution phase with bcc structure,while other alloys with x=2-6 consist of a bcc main phase and a small fraction of C14 type laves secondary phase. The lattice parameter and unit cell volume of the bcc main phase decrease with the increase of the Mn content. It is found that all of these alloys have good activation behaviors and hydriding kinetics. The alloys containing Mn can Absorb hydrogen without hydriding incubation time at 298K and under an initial hydrogen pressure of 4MPa. With increasing the Mn content in the alloys,the hydrogen desorption plateau is flattened,the plateau pressure increases first and then drops. However,the maximum hydrogen Absorption capacity at 298K and the effective hydrogen desorption capacity at 333K decrease gradually with the increase of the Mn content.