Microstructures and hydrogen storage characteristics of (Ti0.1V0.9)(100-x)Fe-x (x=0 similar to 6) alloys

Zheng Fangping,Zheng Chuanxiang,Wang Xinhua,Wang Yaru,Chen Lixin

2006-01-01

Rare Metal Materials and Engineering

Abstract:The phase structures and hydrogen storage characteristics of (Ti0.1V0.9)(100-x)Fe-x (x=0, 2, 4, 6) alloys were investigated systematically. The microstructure analysis shows that all of the alloys consist of a single vanadium-based solid-solution phase with BCC structure. As the Fe content increased, the lattice parameter descends linearly, the unit cell volume also decreased. It is found that all of the alloys have good kinetics behaviors and can absorb hydrogen without any hydrogenation gestation time at 10 degrees C and under an initial hydrogen pressure of 4 MPa. As the Fe content increases from 0 to 6, the activation property of the alloys is improved, the maximum hydrogen absorption capacity at 10 degrees C decreases from 509.5 ml/g to 424.8 ml/g, and the effective hydrogen desorption capacity increases first and then decreases, while the maximum value of 255.6 ml/g is obtained at x=4. Among these alloys studied, the Ti9.6V86.4Fe4 alloy has a good overall property, such as the activation number of 2 cycles, the maximum hydrogen absorption capacity of 494.5 ml/g at 10 degrees C and the effective hydrogen desorption capacity of 255.6 ml/g at 50 degrees C.