Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

LX Chen,J Liu,XH Wang,FP Zheng,FB Dai,CP Chen

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.05.003

2006-01-01

Abstract:The phase structure and hydrogen storage properties of Ti17Cr23V55-xZr5Fex (x = 11 similar to 16) alloys have been investigated systematically. XRD and SEM analysis show that all of the alloys consist of a main phase of V-based solid solution with bcc structure and some secondary phases of sigma-FeCr and Cr2Zr. With the increase of Fe content in the alloys, the abundance and unit cell volume of the bcc main phase decrease, the sigma-FeCr phase content increases, and the Cr2Zr phase content is almost invariable. It is found that all of these alloys have a very good activation behavior and a good kinetic behavior. They are activated during the first hydrogenation time and absorb hydrogen rapidly without hydrogenation gestation time. As the Fe content increases from x = 11 to x = 16, the maximum hydrogen absorption capacity decreases from 268 ml/g to 251 ml/g at 20 degrees C, and the effective hydrogen desorption capacity decreases from 153 ml/g to 137 ml/g at 80 degrees C. The result shows that eliminating the sigma-FeCr phase in the alloy is essential for improving the hydrogen storage ability of these alloys.