Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Hydrogen Storage Properties of FeTi1.3 + X Wt%mm (x = 0.0, 1.5, 3.0, 4.5, 6.0) Hydrogen Storage Alloys

Studies of hydrogen storage properties and absorption-desorption mechanism of FeTi1.3(Mm)y alloy

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Microstructures and hydrogen storage characteristics of (Ti0.1V0.9)(100-x)Fe-x (x=0 similar to 6) alloys

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Hydrogen Storage Properties of Mg-doped Ti 1.2 Fe Alloys Synthesized by Mechanical Alloying

Influence of Fe Content on the Microstructure and Hydrogen Storage Properties of Ti16Zr5Cr22V57−xFex (x = 2–8) Alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Influences of misch metal on hydrogen storage properties of FeTii.3 alloy

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Hydrogen storage performances, kinetics and microstructure of Ti<sub>1.02</sub>Cr<sub>1.0</sub>Fe<sub>0.7-x</sub>Mn<sub>0.3</sub>Al<su b>x</sub> alloy by Al substituting for Fe

Fundamental hydrogen storage properties of TiFe-alloy with partial substitution of Fe by Ti and Mn

Hydrogen Storage Properties of Tixfe+Y Wt.% La and Its Use in Metal Hydride Hydrogen Compressor

Hydrogen storage properties of Ti/TiF3-doping LiAlH4/LiNH2 composites

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Structures and Properties of TiMn2-5x(V4Fe)x(x=0.30, 0.35) Hydrogen Storage Alloys

Hydrogen storage performance of Ti–V-based BCC phase alloys with various Fe content