Influence of Annealing Treatment on the Microstructure and Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application
Langxia Liu,Lixin Chen,Xuezhang Xiao,Chenchen Xu,Jian Sun,Shouquan Li,Hongwei Ge,Lijun Jiang
DOI: https://doi.org/10.1016/j.jallcom.2015.02.138
IF: 6.2
2015-01-01
Journal of Alloys and Compounds
Abstract:The as-cast Ti1.02Cr1.1Mn0.3Fe0.6 alloy for hybrid hydrogen storage vessel application was annealed at different temperatures (873 K, 973 K, 1123 K, 1173 K) for 2 h, and annealed at 1123 K for different time (2, 5, 8 h) respectively, and their microstructure and hydrogen storage properties were investigated systematically. The results show that the as-cast alloy has a single C14 Laves phase, and all annealed alloys consist of a C14 Laves main phase and a secondary phase. After annealing at different temperatures for 2 h, the hydrogen absorption pressure at 298 K decreases, however, the maximum hydrogen storage capacity and desorption pressures at 318 K decrease slightly too. As the annealing time extends, the hydrogen absorption plateau pressure at 298 K and hydrogen desorption plateau pressure at 318 K increase, and the hydrogen desorption capacity increases first and then decreases, which reaches the highest desorption capacity of 1.721 wt.% at the annealing time of 5 h. Among the studied alloys, the alloy annealed at 1123 K for 5 h has the best overall properties for hybrid hydrogen storage application, its hydrogen absorption plateau at 298 K is 29.09 MPa, its hydrogen desorption plateau pressure at 318 K is 45.12 MPa, its hydrogen storage capacity is 1.721 wt.% and its dissociation enthalpy (Delta H-d) is 17.78 kJ/mol H-2. (C) 2015 Elsevier B.V. All rights reserved.