Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6 similar to 1.6) alloys

Du Shuli,Wang Xinhua,Chen Lixin,Li Shouquan,Chen Changpin,Tang Ying,Xiao Xuezhang

2006-01-01

Rare Metal Materials and Engineering

Abstract:The effects of the substitution of Mn with V in the Ti1.0VxMn2-x (x=0.6 similar to 1.6) alloys on the microstructure and hydrogen storage properties were investigated. It was found that the alloys transform from a composition of two phases (Laves and bcc phases) into a single bcc phase gradually as x increasing. The alloys with V content of x >= 1.2 consist of V-based solid solution with single bcc phase when the maximum hydrogen absorption capacity of 3.5wt.% was achieved. However, its activation properties degrade and the hydrogenation saturation time is prolonged due to the lack of the brittle Laves phase. Moreover, the cell volume of the bcc phase expand with the increase of the V content, resulting in the significant decrease of plateau pressure towards smooth and the increase of hysteresis effect of hydriding/dehydriding, but the plateau pressure become flatter.