Hydrogen Storage Properties of La1.8Ca0.2Mg14Ni3 Alloy Prepared by Ball Milling in Different Milling Environments

Linhui Gao,Changpin Chen,Lixin Chen,Qidong Wang,Changyao Wang,Yue An

DOI: https://doi.org/10.1016/j.jallcom.2005.12.067

IF: 6.2

2006-01-01

Journal of Alloys and Compounds

Abstract:The hydriding/dehydriding properties of the La1.8Ca0.2Mg14Ni3 alloy modified by mechanical ball milling for 20h in different environment media, namely under argon, in toluene and in THF, respectively, have been investigated. XRD and SEM results show that the environment media affect the microstructure and surface morphology of the alloy noticeably. For the three environment media used, THF achieved the highest enhancement in hydriding/dehydriding properties. The effect of argon ranked the second and that of toluene the third. But the difference between the second and the third was very small. For the samples milled in THF, the amount of hydrogen absorbed reached 5.1wt.% within 300s at 600K and 4.2wt.% within 600s at room temperature. The amount of hydrogen desorbed reached 5.05wt.% at 613K. The remarkable improvement of the hydrogen storage properties of the ball-milled alloy in different environment media experimented is ascribed to the physical and chemical change of the alloy surface. Most probably are due to the appearance of the active sites and the electron donor–acceptor (EDA) complexes produced by the ball-milling process.