Abstract:Organometallically prepared AlH3 and as-received Al powders were mixed with MgH2 to improve the dehydriding and rehydriding properties of MgH2. Thermal analysis shows that the onset dehydriding temperature of MgH2 is reduced by 55 degrees C (or 25 degrees C) when mixed with AlH3 (or Al). The destabilization of MgH2 is attributed to the formation of Mg-Al alloys through the reaction between MgH2 and Al. Isothermal dehydriding measurements demonstrate that AlH3 and Al both improve the dehydriding kinetic of MgH2 to some extent, and it only takes 44 min for MgH2 + AlH3 (5.4 h for MgH2 + Al) to release 60% of the hydrogen of MgH2 at 300 degrees C, but 8.6 h are required for as-milled MgH2. The apparent activation energy for the dehydriding of MgH2 is reduced from 174.6 kJ mol(-1) for as-milled MgH2 to 154.8 and 138.1 kJ mol(-1) for MgH2 mixed with Al and AlH3 respectively; this is responsible for the improvement in the dehydriding kinetics of MgH2. Despite this, AlH3 is better in destabilizing MgH2 than the as-received Al for the fact that Al* formed in situ from the decomposition of AlH3 is oxide-free on the particle surfaces, which effectively increases the chemical activity of Al*. Furthermore, the brittleness of AlH3 makes it easier to mix MgH2 with AlH3, which would result in uniform distributions of Mg and Al and shortening of the diffusion length. Concerning the reversibility, at 300 degrees C and 5 MPa H-2 and MgH2 are fully recovered in the dehydrided MgH2 + Al, and MgH2 + AlH3 samples after rehydriding for 10 h. The rehydriding kinetic of MgH2 is significantly enhanced for the dehydrided MgH2 + AlH3, but not in the case of the MgH2 + Al.

Hydriding/dehydriding properties of La2Mg16Ni alloy prepared by ball milling in different milling environments

Hydrogen Storage Properties of La2Mg16Ni Alloy Modified by Ball Milling in Benzene

Hydrogen Storage Properties of La1.8Ca0.2Mg14Ni3 Alloy Prepared by Ball Milling in Different Milling Environments

Hydriding Behavior of Magnesium-Based Hydrogen Storage Alloy Modified by Mechanical Ball-Milling

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

The Hydriding and Dehydriding Properties of Some Multicomponent Rare-Earth Magnesium Alloys

Improved hydrogen storage thermodynamics and kinetics of La–Ce–Mg–Ni alloy by ball milling

Effect of ball-milling on the phase structure and hydrogen storage properties of Ti0.9Zr0.1Mn1.5 alloy

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Electrode properties of La2Mg17 alloy ball-milled with x wt.% cobalt powder (x = 50, 100, 150 and 200)

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

Microstructures and hydrogen storage characteristics of nanocrystal/amorphous Mg17Al12 alloy prepared by ball-milling

The Electrochemical Evaluation of Ball Milled MgNi-based Hydrogen Storage Alloys

Synergistic function of milling time and Ni addition on microstructure and hydrogen storage properties of CeMg 12 type materials

Improved Hydrogen Storage Properties of MgH2 by Ball Milling with AlH3: Preparations, De/rehydriding Properties, and Reaction Mechanisms

Microstructure and hydrogen storage property of as-milled La–Y–Mg–Ni alloy

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Electrochemical Performance of the Ball-Milled La2Mg14−xTixNi3 Alloys with Ni Powders (x=1 and 2)

Preparation of Mg2Ni Hydrogen Storage Alloy Materials by High Energy Ball Milling

Effect of Milling Intensity on the Formation of LiMgN from the Dehydrogenation of LiNH2–MgH2 (1:1) Mixture

Effects of ball-milling time and Bi2O3 addition on electrochemical performance of ball-milled La2Mg17+200wt.% Ni composites