Abstract:Heterogeneous W-steel joining components will produce brittle intermetallic compounds (IMCs) and significant residual stress in the interface. Adding a Cu interlayer serves as an effective solution. Nevertheless, the strengthening of W-Cu-steel joints is restricted because W-Cu and Cu-steel are members of binary immiscible and finite solid solution systems. Thus, accomplishing interface alloying by overcoming the positive generating energy of insoluble systems and opening up interatomic diffusion channels is a crucial issue to be addressed. In this work, casting and brazing technologies were incorporated into bonding W-Cu-steel to provide a high temperature field, as well as the dissolving and wetting of Cu-based liquid phase to refractory W. It is shown that the superior tensile strength of the W/Cu castings-steel brazed joints (similar to 264 MPa) was achieved, and the joint survived 1000 cycles of thermal fatigue under 1 MW/m(2). To assess the effects of brazing and casting on the W-Cu-steel joint, a detailed analysis was conducted on the mechanism of atomic diffusion in the joint interface. It is considered that in W-Cu joining, casting provided a higher thermodynamic driving force than brazing, thus achieving better interatomic diffusion and a wider microalloying region. Cu-steel joining achieved good alloying and forming dendritic extensions by intergranular diffusion. Based on the process optimization results, the feasibility of preparing the U-shaped first wall (FW) mock-up with W armor using brazing technology was verified. This study provides a new technological path, offering a major design and manufacturing guide for plasma facing components (PFCs).

High-strength Vacuum Diffusion Bonding of Cu-plated, Sandblasted W and CuCrZr Alloy

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Study on the Microstructure and Properties Evolution of CuCrZr/316LN-IG Explosion Bonding for ITER First Wall Components

Study on interface behavior of Be/CuCrZr alloy by diffusion bonding

Interlocked interface of W–Y2O3/CuCrZr joint obtained by W–Y2O3 surface nanoporosification and Cu magnetron sputtering

Research on Be/CuCrZr Bonding by Hot Isostatic Pressing at Intermediate Temperature

High-strength Diffusion Bonding of Oxide-Dispersion-strengthened Tungsten and CuCrZr Alloy Through Surface Nano-Activation and Cu Plating

Microstructure and mechanical properties of W/Cu vacuum diffusion bonding joints using amorphous Fe–W alloy as interlayer

Diffusion bonding and interface structure of advanced carbide-dispersion-strengthened Cu and oxide-dispersion-strengthened W

Bonding Tungsten, W–Cu-alloy and Copper with Amorphous Fe–W Alloy Transition

Femtosecond Laser Fabricated Micro/nano Interface Structures Toward Enhanced Bonding Strength and Heat Transfer Capability of W/Cu Joining

Experiment and Simulation Investigations on W/Cu Components Prepared by Strong Confinement Thermal Explosive Welding

Improving the Interface Strength and Fatigue Property of W-Cu-steel Brazed Joint Via Induced Interface Alloying

W/Cu Joining Strengthened by Femtosecond Laser Induced Micron-Scale Interface Structure

Comprehensive Enhancement of the Mechanical and Thermo-Mechanical Properties of W/Cu Joints Via Femtosecond Laser Fabricated Micro/nano Interface Structures

Interfacial evolution mechanism of W/Cu explosive welding interface affected by preheating

Tungsten/steel diffusion bonding using Cu/W–Ni/Ni multi-interlayer

Transient thermal shock and helium ion irradiation damage behaviors of ODS-W/CuCrZr joints

Microstructure, residual stresses and mechanical properties of diffusion bonded tungsten–steel joint using a V/Cu composite barrier interlayer

Stable bonding of W and ODS steel fabricated by TLP diffusion technology through inserting a novel composite interlayer Zr/Cu

Recent progress in research on bonding technologies of W/Cu monoblocks as the divertor for nuclear fusion reactors