Preparation and Wear Resistance of Tungsten Carbide Layer at Gray Cast Iron Surface

Shi-li CHENG,Li-sheng ZHONG,Yong-hong FU,Liang-liang WANG
DOI: https://doi.org/10.11973/jxgccl201602004
2016-01-01
Abstract:Tungsten carbide (WC)layer was in-situ synthesized at the surface of HT300 gray cast iron by combination of casting-infiltration and heat treatment process.The microstructures and wear resistance of the WC layers were studied by scanning electron microscopy,X-ray diffraction and pin disk abrasive wear test.The wear mechanism was also analyzed.The results show that the WC layer with thickness of 1 12 μm was formed on the surface of the gray cast iron.The relative wear resistance of the WC layer first increased then decreased with the increase of loads.When the load was 1 5 N,the relative wear resistance of the WC layer was better than that of the gray cast iron.Under the heavy load,the wear-out failure of the WC layer mainly ascribed to particles′ squeezing fracture and partial peeling,meanwhile sheet-like wear debris was generated.
What problem does this paper attempt to address?