Abstract:An as-cast chromium white cast iron alloy with chromium (Cr) content of 0 wt%, 1 wt%, 2 wt%, 3 wt%, and 4 wt % was prepared via metallurgical smelting and casting processes. The effects of Cr content on the toughness, hardness, and microstructure of (Fe, Cr)(3)C carbides was evaluated. The results revealed that the microstructure of the as-cast alloys is mainly composed of bulk carbide and the pearlite matrix. The carbide in the alloy without added Cr, i.e., eutectic Fe3C, was characterized by a continuous network structure. With the addition of Cr atoms, the Fe3C-type carbide was transformed into (Fe, Cr)(3)C, leading to a gradual increase in the fracture toughness of the carbide. This may have resulted from the incorporation of Cr into Fe3C and the consequent crystal-structure transformation of the carbide. When the Cr content of the carbide was lower than the saturation level (<2 wt%), the microhardness of the carbide in the as-cast alloy increased significantly. This resulted from an increase in the number of strong (Fe-Cr) metallic bonds in the carbide. However, for Cr content exceeding 2 wt%, the microhardness increased only slightly. Changes in the mechanical properties of the carbides resulted in improved wear resistance of the materials and changes in the wear mechanism of the carbides. At low Cr content, the wear failure of the carbide was characterized mainly by brittle fracture and peeling. With improvement in the toughening performance, microcutting became the main wear failure mechanism of the carbides and exerted a significant blocking effect on the silicon oxide abrasive.

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron

Effect of the Cr/C on the Microstructure and Properties of High Chromium Cast Iron Containing 31% Cr

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Effect of Cr Addition on the Microstructure and Abrasive Wear Resistance of WC-reinforced Iron Matrix Surface Composites

Effect of Chromium-Induced (fe, Cr)3C Toughness Improvement on the Two-Body Abrasive Wear Behaviors of White Cast Iron

Effect of W Content on Microstructure and High Temperature Tensile Properties of High Tungsten Cast Superalloy

Effect of Carbon Content on Microstructure and Properties ofCr25 High-Chromium Cast Steel

Effect of Carbon Content on Three-body Abrasive Wear Characteristics of 28Cr-3Ni Cast Alloys

Investigation on Microstructure and Wear Resistance of the New CrWMoV High-Alloy Wear Resistant Cast Iron

Influence of Heat-Treatment on the Microstructure and Properties of Hypereutectic High-Chromium Cast Iron Containing Ti

Effect of Chromium Content on Microstructure, Hardness, and Wear Resistance of As-Cast Fe-Cr-B Alloy

The influence of different content of Cr on microstructure and properties of WC-Co cemented carbide

Effect of titanium on the microstructure of hypereutectic high-chromium cast iron

Effect of Tungsten Addition on Continuous Cooling Transformation and Precipitation Behavior of a High Titanium Microalloyed Steel

Effect of Titanium on the As-Cast Microstructure of Hypereutectic High Chromium Cast Iron

The Influence of Ni Content on the Microstructure and Impact Wear Resistance Performance of High-Chromium Casting Infiltration Coating

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

Effect of Cr Content on the Microstructure of Casting Infiltration Layers: Simulations and Experiments

Effect of Additive Amount of Cr on Microstructure and Properties of Wc-9ni Cemented Carbides