Abstract:Millimeter-sized ZTA (zirconia toughened alumina) particles + WC (tungsten carbide) particles reinforced hypereutectic high chromium cast iron (H-HCCI) composites were prepared by liquid phase sintering. The volume fraction, stacking method and sintering process of the reinforced particles in the composites were designed. The interfacial bonding mechanism between the reinforcements and the matrix in the composites was systematically discussed. The results show that when the sintering temperature is 1380 °C, the volume percentage of ZTA particles, WC particles and H-HCCI is set to 10, 30 and 60%, respectively, and the reinforced particles are mixed and stacked, the prepared sample has the best performance. The average nano-hardness of ZTA particles, the interface layer between ZTA particles and H-HCCI matrix, WC particles and H-HCCI matrix in the composites are 20.83, 19.08, 23.33 and 16.39 GPa, respectively. The Young's moduli of each component in the composites are 330.56, 289.41, 300.68 and 232.11 GPa, respectively. Based on the results of friction and wear experiments, the average wear depth of ZTA particles is 6.589 μm, the average wear depth of WC particles is 4.872 μm, and the average wear depth of H-HCCI matrix is 9.802 μm.Through performance testing, it was found that the hybrid reinforced composites showed excellent comprehensive properties. This paper provides theoretical support for multiphase reinforced composites, and proposes a new method for preparing ZTA particle reinforced metal matrix composites, which realizes the metallurgical interface bonding between ceramics and metals.

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Recent Developments in Fabrication of Ceramic Particle Reinforced Iron Matrix Wear Resistant Surface Composite Using Infiltration Casting Technology

Microstructure and wear characteristics of ATZ ceramic particle reinforced gray iron matrix surface composites

Fabrication of ZTA/High Chromium Cast Iron Matrix Composites and Its Abrasive Wear Resistant

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

Interfacial Characteristics and Wear Resistance of WCp/White-Cast-Iron Composites

Interfacial characteristics and wear resistance of WCp/white-cast-ion composites

Study on Surface WC Particle Reinforced Chromium Abrasion Resistant White Cast Irons Composite

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

Microstructure and Wear Behavior of High-Cr WCI Matrix Surface Composite Reinforced with Cemented Carbide Rods

Interfacial characteristics and wear performances of iron matrix composites reinforced with zirconia-toughened alumina ceramic particles

Wearing and interfacial characterization of zirconia toughened alumina reinforced high chromium cast iron composites in an actual working condition

Mechanical Properties and Wear Resistance of ZrO2 Particulate-Reinforced Composite Layer on Compacted Graphite Cast Iron Processed by Selective Laser Alloying

Interface Structure and Wear Behavior of Cr26 Ferrous Matrix Surface Composites Reinforced with CTC P

The Development of High Carbon Chromium Iron Power Reinforced Steel Matrix Wear-resistant Surface-layer Composite

Elucidation of Abrasive Wear and Slurry Erosion Behavior of Fe Matrix Composites Reinforced with Metallic Coating Modified ZTAP Ceramics

Interfacial Bonding and Abrasive Wear Behaviours of the Iron Matrix Composites

Preparation of ZrO 2-Al 2O 3 honeycomb ceramic reinforced high Cr cast iron matrix composites by composite processing

General Process for in Situ Formation of Iron-Matrix Surface Composites Reinforced by Carbide Ceramic