Abstract:WC/Fe matrix composites with mass fractions of 30–50 wt% were prepared by gravity casting and infiltration, and the phase composition, microstructure, friction and wear properties of the composites were studied. In addition, the mechanism of the effect of the change of WC mass fraction on the structural evolution and wear properties of the composites was particularly investigated. The results show that the composites are mainly composed of WC, α-Fe, W 2 C, Fe 6 W 6 C, and M 7 C 3 phases. With the increase of WC mass fraction, the microstructure of the composite shows different results, WC particles start to dissolve under the action of high temperature melt, W elements solidly dissolve into the matrix and precipitate into fishbone structure carbide. As the content of WC particles in the prefabricated body increases, the C atoms around the WC particles react with the dissolved W atoms, and due to the cooling of the metal liquid, the energy transferred between the WC and the metal liquid does not make it melt completely before solidification occurs, and the metallurgical reaction between the WC particles and the substrate occurs and produces a dense interface. The WC/Fe matrix composites showed a trend of increasing and then decreasing with the increase of WC content and friction coefficients of 0.36, 0.52, and 0.26. The wear rates were 1.52(mm 3 /N-m) × 10 −5 , 1.24(mm 3 /N-m) × 10 −5 , and 1.57(mm 3 /N-m) × 10 −5 , which showed the opposite trend with the friction coefficients, and the wear rates were compared with the morphology. When the composite was added with 40% WC, the wear rate increased by 27% compared with other parameters. It shows that it has good wear resistance.

Study of Abrasive Wear Resistant of WC Particle Reinforced Chromium White Cast Irons Matrix Composite

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Effect of In-Situ (ti&w)c Multiphase Particles on Three-Body Abrasive Wear of High Chromium Cast Iron

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effect of WC mass fraction on the microstructure and frictional wear properties of WC/Fe matrix composites

Interface microstructure and abrasive wear properties of WC-iron matrix composites with Ni, Mo, Fe added to the preforms

Wear Behavior of WC/GCr15 Steel Composite Prepared by Electroslag Melting and Casting

Abrasive wear behavior and mechanism of high chromium cast iron

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Microstructure and Wear Resistance of WC and High Chromium Cast Iron Hardfacing Layers

Microstructural evolution and performance analysis of WC-11Co reinforced iron matrix composites

Spark Plasma Sintering Preparation of Tungsten Carbide-Reinforced Iron-Based Composite Materials: Wear Resistance Performance and Mechanism

The Effects of WCp Contents on Wear Resistance of Electroslag WC/GCr15 Steel Composites

Effect of Carbon Content on Three-body Abrasive Wear Characteristics of 28Cr-3Ni Cast Alloys

Friction and wear characteristics of plasma-sprayed WC coatings in dliding against GCr15 steel

Interfacial bonding and wear behavior of macroscopic TiC particulates reinforced iron-based composites fabricated by infiltration casting process

Study of the Erosive-abrasive Wear Resistance of Fe-14%Cr-2.8%C High Chromium Cast Iron

Study on the abrasive resistance of Ni-based coatings containing WC hard phase

Effect of WC-10Co-4Cr Reinforcement Amount on Wear and Corrosion Resistance of Fe-Based Amorphous Coatings