Abstract:Erosion wear is a common and serious problem in slurry transportation field. In order to improve the erosion wear performance of high chromium cast iron (HCCI), a new type of high chromium cast iron with 0.38% nitrogen (HCCI-N) was fabricated by vacuum induction positive pressure melting furnace under 0.4 MPa nitrogen partial pressure on the basis of the established pseudo-binary phase diagram of (Fe-27Cr-2.2C)-N alloy system. The microstructure and erosion wear behavior of HCCI-N were researched in alkaline sand slurry. Results show that the microstructure of HCCI-N has the characteristics of multi-scale and multi-type carbides, including eutectic M7C3 (∼20μm), secondary M23C6 (∼2μm) and Cr2C (∼1μm), distributed in matrix composed of martensite and austenite. A sandwich structure of M7C3-ferrite-martensite was formed at the interface of eutectic M7C3. The nitrogen element is mainly distributed in matrix. The Cr2C (-1011) is coherent with Martensite (110). The erosion wear is caused by the synergy of corrosion and wear. The pure wear rate (Ve) of HCCI-N accounts for 71%∼93% of total erosion wear rate (Vt) under different test conditions, indicating that wear loss mainly results from the mechanical action under alkaline sand slurry. Nevertheless, the synergism rate of corrosion and wear (Vs) is also significant to Vt, which accounts for 7%-29% of Vt for HCCI-N relative to 13%-31% of HCCI. The HCCI-N has more excellent erosion wear resistance compared with that of HCCI under all the test conditions, and the optimal wear resistance of HCCI-N is 1.34 times that of HCCI. The nitrogen and chromium dissolved in matrix improves corrosion resistance, and reduces the synergistic rate of corrosion and wear. Multi-scale carbide strengthens the matrix and resists mechanical wear. The combined action of the two factors makes the HCCI-N have excellent erosion wear resistance.

Study of the Erosive-abrasive Wear Resistance of Fe-14%Cr-2.8%C High Chromium Cast Iron

Abrasive wear behavior and mechanism of high chromium cast iron

Corrosion Wear of Hypereutectic High Chromium Cast Iron: A Review

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Microstructure and abrasive wear properties of high-vanadium-chromium wear resistant alloy

Microstructure and erosion wear properties of high chromium cast iron added nitrogen by high pressure in alkaline sand slurry

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Microstructure and Wear Resistance of WC and High Chromium Cast Iron Hardfacing Layers

Refinement of primary carbides in hypereutectic high-chromium cast irons: a review

Fabrication and abrasive wear property of high chromium cast iron with high vanadium and high nitrogen content (HCCI-VN)

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Tribology in mining: Highlights in iron ore abrasiveness

A Study On The Dynamic Characteristics Of Abrasion For High-Chromium Alloys

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Optimizing heat treatment and wear resistance of high chromium cast irons using computational thermodynamics

Effects of Heat Treatment and Erosion Particle Size on Erosion Resistance of a Hypereutectic High-Chromium Cast Iron

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Heat Treatment Effect on the Microstructure and Tribological Behaviour of a High Chromium Cast Iron with 0.5% of Niobium

Influence of Niobium Addition on Microstructure and Machinability of High Chromium Cast Iron

Fabrication of a Composite Material of High‐Chromium Cast Iron Dispersed in Low‐Carbon Steel by Hot‐Rolling Process

Effect of interlayer temperature and extremely low terminal cooling temperature on the microstructure and wear resistance of Fe-based hardfacing alloy