Abstract:The components made out of hypereutectic high-chromium cast iron (HCCI), featured with high abrasion resistance and hardness, are usually subjected to destabilization treatment before use, to improve their hardness and wear resistance by destabilizing the retained austenite which transforms to martensite. This study investigates the effects of destabilization and tempering heat treatment on the microstructure and mechanical properties of an HCCI with and without modification of primary carbides. For the unmodified HCCI, the destabilization simultaneously increased both hardness and the transverse rupture strength (TRS). Increasing the destabilization temperature from 970 to 1090 °C led to a marginal decrease in hardness and slight increase in TRS. Destabilization at 1090 °C increased the transverse rupture strength (TRS) by 54% compared to the as-cast HCCI without reduction in wear resistance due to the coarsening of the secondary carbides. In addition, tempering within a temperature range from 200 to 280 °C after destabilization at 1090 °C led to a slight decrease in hardness, but an increase in TRS and wear resistance. Further increasing the tempering temperature to 310, 340 and 400 °C did not vary the properties. Tempering at 280 °C after destabilization at 1090 °C enabled more than 85% increase in TRS compared to the as-cast HCCI. The influence of destabilization temperature on the TiB 2 -modified HCCI is similar to the unmodified alloy. But, tempering after destabilization at 1090 °C decreased both hardness and TRS without significant variation of wear resistance even though a TRS peak was obtained at 310 °C tempering. Hence, to achieve the best performance an optimized heat treatment for the unmodified HCCI is destabilization at 1090 °C followed by tempering at 280 °C. For the TiB 2 -modified HCCI, tempering is not needed. Rationalizations of the mechanical properties are also discussed in terms of microstructure.

Heat Treatment Effect on the Microstructure and Tribological Behaviour of a High Chromium Cast Iron with 0.5% of Niobium

Effect of niobium addition on the properties and microstructure of a high chromium cast iron alloy

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Influence of Niobium Addition on Microstructure and Machinability of High Chromium Cast Iron

Effect of Heat Treatment Temperature on the Microstructure, Wear and Friction of Ni–Nb–V Alloyed Manganese Steel

Influence of Niobium Content on the Mechanical Properties and Abrasion Wear Resistance of Heat-Treated High-Chromium Cast Iron

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Ti-bearing Hypereutectic High Chromium White Cast Iron

Effect of Heat Treatment on Microstructure and Properties of Wear Resistant Cast Fe-C-B Alloy

Effect of Niobium and Heat Treatment on the Microstructure and Mechanical Properties of SAE 8620 Steel

Characterisation and machinability of high chromium hardened white cast iron with and without the addition of niobium

The Effect of Tempering Temperature on Microstructure and Wear Behavior of Tungsten and Boron Alloyed Ni-Hard 4 White Cast Irons

Microstructure Evolution and Mechanical Properties of High Nb-TiAl Intermetallic Compounds during Heat Treatment

Effects of niobium and heat treatment on microstructure and mechanical properties of low carbon cast steels

Effects of destabilization and tempering on microstructure and mechanical properties of a hypereutectic high-chromium cast iron

Normalizing Temperature Influence on the Microstructure Characteristics, Mechanical and Wear Performance of a Novel High Chromium Cast Iron

Effect of Austempering Conditions on the Corrosion Behavior of HSADI Alloyed with Niobium

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Effect of isothermal temperature and load on wear of nanobainitic cast steel

Effect of Heat Treatment on the Microstructural Heterogeneity and Abrasive Wear Behavior of ASTM A128 Grade C Steel

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Effects of Nb Additions and Heat Treatments on the Microstructure, Hardness and Wear Resistance of CuNiCrSiCoTiNbx High-Entropy Alloys