Abstract:Carbide-free nano-bainite steel holds significant potential for applications in mining as an ultra-high strength wear-resistant steel, but the wear mechanisms are not yet fully understood. This study aims to explore the effect of austempering temperature on microstructure, mechanical properties and wear resistance of carbide-free nano-bainitic steel. The relationship between the content and mechanical stability of retained austenite (RA) and mechanical properties was investigated to elucidate the mechanisms of pin-on-disc wear and impact wear. The results show that in the range of M s ∼300 °C, the phase transformation incubation period and completion time significantly increase with decreasing austempering temperature, which is mainly related to higher phase transformation driving force resulting from a larger subcooling degree and slow growth of carbon content in RA. Optimal strength and hardness of 2099 MPa and 615 HBW, respectively, are achieved after austempering at 210 °C for 83 h. Austempering at 270 °C for 11 h yields the best balance of strength and plasticity, with a strength-plasticity product of 28.8 GPa%. The micro-cutting mechanism of pin-on-disc wear leads to serious weight loss. The RA with poor mechanical stability accelerates the stress-induced martensite transformation, while internal stress support due to volume expansion reduces the penetration depth of abrasive particles. The weight loss in impact wear is primarily caused by shedding due to fatigue failure. With the increase of RA content and mechanical stability, the persistent stress-induced martensite transformation effectively hinders micro-crack propagation, thereby enhancing impact wear resistance.

Effect of isothermal temperature and load on wear of nanobainitic cast steel

Effect of Nanobainite Content on the Dry Sliding Wear Behavior of an Al-Alloyed High Carbon Steel with Nanobainitic Microstructure.

Effect of Heat Treatment Temperature on the Microstructure, Wear and Friction of Ni–Nb–V Alloyed Manganese Steel

Heat Treatment Effect on the Microstructure and Tribological Behaviour of a High Chromium Cast Iron with 0.5% of Niobium

High Temperature Sliding Wear Behaviors of Ion Plating Tin Composite Coating with Ion Nitriding As Interlayer on Hot Work Die Steel

Effect of Austempering Temperature on Microstructure Evolution, Mechanical Properties and Wear Resistance of Carbon-free Nano-bainite Steel

Influence of Ni content on impact-abrasion wear resistance of medium-carbon low alloy cast steel

Effect of Heat Treatment on Tribological Properties of Ni-B Coatings on Low Carbon Steel: Wear Maps and Wear Mechanisms

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Sliding wear resistance and worn surface microstructure of nanostructured bainitic steel

Effect of Si on Wear Resistance of Bainitic Cast Steel under High Stress Impact

The Microstructure Transformations and Wear Properties of Nanostructured Bainite Steel with Different Si Content

Effect of Temperature and Load on Tribological Behavior in Laser-Cladded FeCrSiNiCoC Coatings

Wear behavior of bainite ductile cast iron under impact load

Comparison on Wear Resistance of Nanostructured Bainitic Bearing Steel with and Without Residual Cementite

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Effects of Temperature on the Tribological Properties of NM600 under Sliding Wear

The effect of temperature on the unlubricated sliding wear of 5 CrNiMo steel against 40 MnB steel in the range 400–600°C

Effect of heat treatment on mechanical and stirring wear properties of low temperature bainite steels

Wear Performance Under Dry and Lubricated Conditions of Post Boriding Heat Treatment in 4140 Steel

The Effect of Tempering Temperature on Microstructure and Wear Behavior of Tungsten and Boron Alloyed Ni-Hard 4 White Cast Irons