Abstract:The purpose of the investigations was to study systematically the effects of different tempering temperatures on the microstructure, hardness and wear resistance of low‐silicon hypereutectic high‐chromium cast iron. It is expected to provide theoretical support for the development of tempering processes for this material. High‐chromium cast iron is a good wear‐resistant material. Its heat treatment regime has an important influence on the evolution of its microstructure and properties. This study investigates the microstructural attributes and properties of Fe–4.0 C–35.0Cr–0.5Si (wt.%) low‐silicon hypereutectic high‐chromium cast iron subsequent to quenching at 1050 °C, followed by tempering at diverse temperatures. The microstructure was examined using optical microscopy, scanning electron microscopy, and X‐ray diffractometry across varied tempering conditions. Furthermore, microhardness and wear resistance were conducted via a microhardness tester and a wear testing machine. The results show that the quenching heat treatment promotes the transformation of the matrix from austenite to martensite, while also promoting the precipitation of secondary carbides of M23C6‐type. The subsequent tempering heat treatment engenders transformations involving retained austenite to martensite, amplifies the precipitation and enlargement of secondary carbides, and induces martensite decomposition. As the tempering temperature increases, primary and eutectic carbides exhibit minimal changes, while the secondary carbide morphology evolves from granular to reticular. The matrix composition predominantly comprises martensite, interspersed with a minor fraction of austenite. It is worth noting that the alloy has the highest hardness and wear resistance after quenching at 1050 °C and then tempering at 400 °C.

Effects of Heat Treatment and Erosion Particle Size on Erosion Resistance of a Hypereutectic High-Chromium Cast Iron

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Study of the Erosive-abrasive Wear Resistance of Fe-14%Cr-2.8%C High Chromium Cast Iron

Effect of different abrasive particle hardness on the erosion resistant performance of alpha-Al2O3 ceramics

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

Abrasive wear behavior and mechanism of high chromium cast iron

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Erosion-Wear Property of α-Al2O3 Structure Ceramics with Different Experiment Parameters

Influence of Investment Casting Manufacturing Conditions on As-Cast Microstructure and Erosive Wear Resistance of 26%Cr Cast Iron

Optimizing heat treatment and wear resistance of high chromium cast irons using computational thermodynamics

Corrosion Wear of Hypereutectic High Chromium Cast Iron: A Review

Effect of Abrasive Particle Size on Anti-Abrasion Performance of Si3N4 Ceramics

Microstructure, mechanical and erosion wear analysis of post heat treated iron alloy based coating with varying chromium

Experimental investigation of low velocity and high temperature solid particle impact erosion wear

Influence of microstructure on the erosion and erosion–corrosion characteristics of 316 stainless steel

Study on Erosion Resistance of Structural Ceramics

Abrasive Wear Resistance of Nodular Cast Iron After Selected Surface Heat and Thermochemical Treatment Processes

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

The effect of heat treatment and impact angle on the erosion behavior of nickel-tungsten carbide cold spray coating using response surface methodology

Current insights into the factors affecting the erosion behaviour of iron alloy based coating materialEinflussfaktoren auf das Erosionsverhalten von Beschichtungswerkstoff aus Eisenbasislegierung

Heat Treatment Effect on the Microstructure and Tribological Behaviour of a High Chromium Cast Iron with 0.5% of Niobium