Microstructure and mechanical properties of 2.5D curved shallow-crossing linking SiCf/SiC composites fabricated by chemical vapor infiltration

Yue LI,Ruiqian ZHANG,Ping YANG,Zhaoke CHEN,Zongbei HE,Xiang XIONG

2018-01-01

Abstract:The tubular SiCf/SiC composite materials were prepared by depositing SiC-PyC-SiC multi-interlayers on the SiC fibers with 2.5D curved shallow-crossing linking structure densified with SiC matrix using CH3SiCl3-H2-Ar system by chemical vapor infiltration (CVI). The phase composition, microstructure, axial compression, radial crushing and circumferential tension and fracture morphology of SiCf/SiC composites were investigated. The results show that SiCf/SiC composites are mainly composed of SiC fiber, SiC-PyC-SiC multi-interlayers and SiC matrix. In the SiC-PyC-SiC multi-interlayers, the thickness of PyC interlayers is 700-800 nm, the thickness of SiC interface is 400-500 nm, and SiC matrix is mainly β-SiC phase. After densification, the density of SiCf/SiC composites is 2.50-2.58 g/cm3, and the porosity is 7.70%-9.10%. The axial compressive strength of SiCf/SiC composites is 53.2 MPa, and the radial crushing strength is 38.18 MPa. Compression is expressed as a shear failure in the 45° direction with the horizontal plane while it is broken into pieces during crushing test. The fiber pull-out phenomenon can be observed obviously at the fracture, but the pull-out is not long and exhibits a typical pseudo ductility feature. The circumferential tensile strength of SiCf/SiC composites is 12.8 MPa. The fracture is relatively flat, and the phenomenon of fiber pull-out is not obvious, which indicates that it is brittle fracture.