Abstract:Bimetallic composite pipe is composed of the outer layer (carbon steel or low alloy steel pipe) and the inner layer (high alloy corrosion-resistant steel pipe). Generally, when composite pipes can only be welded on one side due to their small diameter, high-alloy welding materials are usually adopted for the whole weld. In this case, the butt welding of L415/316L bimetal mechanical lined pipe adopts the welding sequence of sealing welding-root welding (inner layer)-transition welding-filler and cover welding (outer layer). In order to reduce welding material costs, low-alloy welding material E71T8-Ni1J is used for the outer layer. As a result, cracks at the mechanical joint between the inner layer and the outer layer after welding were found for Φ355 × (11 + 2)mm L415/316L bimetal mechanical lined pipe. Therefore, in this paper, optical microscope (OM) and electron probe micro-analyzer (EPMA) were used to analyze the weld microstructure and the element distribution near the crack, and the hardness of the welded joint was determined by Vickers hardness tester. Meanwhile, the finite element numerical simulation was used to analyze the residual stress near the mechanical joint between the inner and outer layers of composite pipes with different diameters. The results show that the pipe diameter affects the welding residual stress. The welding residual stress of Φ355 × (11 + 2)mm and Φ508 × (16 + 2)mm composite pipes is 301 MPa. There are two factors for the occurrence of cracks at the mechanical joint of Φ355 × (11 + 2)mm composite pipe. The mechanical factor is that the existence of stress concentration. The microstructure factor is the formation of lath martensite and upper bainite. The root cause of weld failure: the welding process was formulated or operated irregularly. The sealing welding layer should be originally austenite. Due to remelting, lath martensite and upper bainite are formed at the sealing welding layer.

Types and Cause of Cold Bending Crack Defects of Welded Pipe

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Experimental Study on the Causes of Cracking of High-Strength Steel During Bending

Effect of Welding Defects on Mechanical Properties of Welded Joints Subjected to Temperature

Cracking Reasons of X70 Steel Submerged Arc Weld Pipe during Guide-Bend Test

Residual Stress Induced by Phase Transformation and its Role in the Delayed Cracking Performance of 22MnB5 Hot Roll Bending Pipes

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Cause Analysis and Preventive Measures against Cracks in 15Cr1Mo1V Steel Welded Joint in Service

Analysis on Cracking of a Pipeline Steel Pipe during Hydraulic Burst Test

Explosion Cracking Analysis of Sulfur Resistance Induction Heat Bend Pipe

Failure analysis of L415/316L composite pipe welded joint

3- Point Bending Test of X70 Pipeling Steel with V Notch along Different Orientation

Segregationand Sulphide Inclusions Influence on Cracking of Cold-formed for 610L

Root Cause Analysis for Cracked Pipe in Auxiliary System in Nuclear Power Plant

Cold bending effect on residual stress, microstructure and mechanical properties of Type 316L stainless steel welded joint

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment

Failure analysis of fillet weld crack in linepipe

Experimental study on fracture toughness of high-strength structural steel and its butt weld

Crack Tip Opening Displacement of X100 Sawl Pipe

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Cracking Analysis on Water Cooling Wall Pipe in Power Plant