3- Point Bending Test of X70 Pipeling Steel with V Notch along Different Orientation

杨政,郭万林,董蕙茹,路民旭,赵新伟

DOI: https://doi.org/10.3969/j.issn.1001-4837.2002.12.005

2002-01-01

Abstract:The effects of thickness, notch orientation and delamination on the initial cracking and total works of X70 pipeline steel samples with V notch were investigated experimentally by use of the 3-point bending test in -60℃, -20℃ and 20℃. The couple effect of delamination cracks, thickness, notch orientation and temperature was discovered. The mechanical behaviors of X70 pipeline steel vary with the change of orientation. The failure model is different as the notch orientation of sample changes. Decreases of effective thickness can increase the initial cracking and total works due to delamination crack as the notch direction of sample is along the thickness. The delamination crack perpendicular to the damage face also can increase the initial cracking and total works as the notch direction of sample is along the plate surface. The reason of delaminating crack is the slice defect and the stress state of sample. The delamination crack has certain direction, and the number of the delamination crack has relation to the temperature. The initial cracking and total works of the thick samples are less than the one of the thin samples at the lower temperature. The initial cracking and total works of the thick samples are equal to the one of the thin samples at the higher temperature and it has no relation to the thickness of samples probably.