Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Effects of Thickness and Delamination on Fracture Toughness of X60 Pipeline Steel

Investigation on Failure Mode of Short Carbon Fiber Reinforced Thermoplastic Composites Joints of Non-metallic Pipeline

Study on TRIP Effect of X65 Pipeline Steel

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

The Fatigue Crack Initiation Life of X60 Pipeline Steel after Pre-tension Deformation

Study on Fracture Behavior and Toughening Mechanisms of Ultra-High-Strength Pipeline Steel

Effect of through-thickness microstructure inhomogeneity on mechanical properties and strain hardening behavior in heavy-wall X70 pipeline steels

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Fracture Response of X80 Pipe Girth Welds under Combined Internal Pressure and Bending Moment

Thickness effect on the ductile fracture properties of the vessel steel with small punch testing techniques

Effects of in-service strain on girth weld failure of an X80 pipeline

Fracture behavior analysis of X80 pipelines welded joints with unequal wall thickness

Fatigue Crack Propagation of X60 Pipeline Steel after Pre-tension Deformation

The Toughness-Induced Crack Deceleration Mechanism on Ultra-High Pressure Steel Gas Pipelines

Effect of plastic pre-strain on the fatigue properties of welded joints of X80 LSAW pipes

Dynamic Ductile Fracture Toughness Test and Numerical Simulation for Ultra-High Pressure Gas Pipelines

Size effects on the ductile/brittle fracture properties of the pressure vessel steel 20 g

Investigating variations in hydrogen-assisted crack propagation of X52 pipeline steel with different microstructural characteristics

Full-scale experimental investigation of the fracture behaviours of welding joints of APL X80 wide plate based on DIC technology

Effects of Hydrogen and Specimen Thickness on Fracture Toughness of Ferritic Steel Welded Joint

Stress–Strain Analysis of a Pipeline With Inner and Outer Corrosion Defects