Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Full-scale experimental investigation of the fracture behaviours of welding joints of APL X80 wide plate based on DIC technology

DIC/DSI Based Studies on the Local Mechanical Behaviors of HR3C/T92 Dissimilar Welded Joint During Plastic Deformation

Fracture behavior analysis of X80 pipelines welded joints with unequal wall thickness

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading

Investigation of the tensile strain response of the girth weld of high-strength steel pipeline

Fracture Response of X80 Pipe Girth Welds under Combined Internal Pressure and Bending Moment

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

A Damage Mechanics based Evaluation of Dynamic Fracture Resistance in Gas Pipelines

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Effects of in-service strain on girth weld failure of an X80 pipeline

Dynamic fracture study by an experiment/simulation method for rich gas transmission X80 steel pipelines

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Study on the Synergistic Effect of Welding Residual Stress and Hydrogen Diffusion on Fatigue Crack Growth of X80 Steel Pipeline

Experiment on the Fracture Toughness of Weld Joint of X70 Pipeline Steel

Welding residual stress analysis of the X80 pipeline: simulation and validation

Fracture Toughness Investigation of X100 Longitudinal Submerged Arc Welded Pipe Via Crack Tip Opening Displacement Test

Failure analysis of fillet weld crack in linepipe

Effect of root welding heat input on microstructure evolution and fracture mechanism in intercritically reheat-coarse grained heat-affected zone of X80 pipeline steel

Fracture driving forces of cracked girth welds with mechanical heterogeneity for X80 pipes