Abstract:Modern micro-alloyed, control-rolled TMCP steels generally have good strength, high toughness, and good weldability. However, these valuable properties come along with certain undesirable features, such as low strain hardening (high yield to tensile ratio), low ductility as measured by uniform elongation (elongation at ultimate tensile strength), and possible heat-affect-zone (HAZ) softening due to reduced hardenability. These undesirable features are particularly detrimental in strain-based design of pipelines. Although the phenomenon of HAZ softening has been known for a long time, the impact of the HAZ softening on the integrity of pipeline girth welds was not well understood. The objective of this work was to understand the impact of HAZ softening on girth weld integrity. Finite element analysis was conducted to investigate the effects of HAZ softening on crack driving force and strain concentration in girth welds under longitudinal tensile loading. The material properties of WM and BM were obtained from an X100 girth weld. The HAZ was modeled as a functionally graded material based on its measured hardness. The models contained surface-breaking defects located at the fusion boundary simulating lack-of-sidewall fusion defects. The analysis results showed that increased CTOD driving force can be expected due to HAZ softening. The extent of increase is positively related to the width and degree of softening of the HAZ. On the other hand, weld strength overmatch reduces the total CTOD driving force. The strain concentration in the softened HAZ circumferentially remote from a surface-breaking defect was small. However, high strain concentration existed over the circumference covering the length of the defect. This concentration was primarily attributable to the existence of the defect and secondarily to the HAZ softening. One significant result from this work was that the relative increase in CTOD driving force and strain concentration due to HAZ softening was independent of defect size. In other words, on a relative basis, HAZ softening was no worse on large defects than on smaller defects. This result should be helpful in rationalizing the effects of HAZ softening for defects of various sizes that exist in field applications. Non-symmetrical crack-tip deformation occurred with softened HAZ. A large proportion of the crack-tip deformation was located in the HAZ. The magnitude of non-symmetric deformation increased with the increase of HAZ width and degree of softening. Even higher degree of non-symmetric deformation occurred with the increase of weld overmatching level. The structural significance of reduced total CTOD driving force and increased un-symmetric deformation at the crack tip due to weld strength overmatch warrants further study. The reduction in total CTOD driving force alone does not necessarily results in a higher level of weld integrity if the “intrinsic” toughness of the HAZ is substantially lower than the weld metal.

Fracture driving forces of cracked girth welds with mechanical heterogeneity for X80 pipes

Correlation Between Heterogeneous Micromechanical Properties and Fracture Toughness in X80 Girth Weld

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Fracture behavior analysis of X80 pipelines welded joints with unequal wall thickness

Numerical study on the strain capacity of girth-welded X80 grade pipes

Simultaneously enhancing strength and fracture toughness via tailoring the microstructure in X80 girth weld metal

Significance of Haz Softening on Strain Concentration and Crack Driving Force in Pipeline Girth Welds

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

Fracture Response of X80 Pipe Girth Welds under Combined Internal Pressure and Bending Moment

FRACTURE TOUGHNESS OF WELDED JOINTS OF X100HIGH-STRENGTH PIPELINE STEEL

Research on the fatigue properties of sub‐heat‐affected zones in X80 pipe

Role of microstructure heterogeneity on hydrogen-assisted fracture toughness degradation of X80 weld metal in H 2 S-saturated solution

Experimental Investigation of Fatigue Behaviour for Welded Joint with Mechanical Heterogeneity

Application of Constraint-Sensitive Fracture Mechanics to the Assessment of Girth Weld Integrity

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading

Numerical Investigation of the Influence of Ultimate-Strength Heterogeneity on Crack Propagation and Fracture Toughness in Welded Joints

Fracture Toughness Investigation of X100 Longitudinal Submerged Arc Welded Pipe Via Crack Tip Opening Displacement Test

Investigation of the tensile strain response of the girth weld of high-strength steel pipeline

Study on Softening in HAZ and Its Influence on Welded Joints of X70 Pipeline Steel

Effect of Strength Mismatch on Ductile Fracture Behavior of Welding Pipe

Analysis of Crack Propagation of Annular Butt Weld and Distribution of Weld-Induced Residual Stress