Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

The 3-Point Bending Fracture Test of X70 Plpeline Steel Samples with V Notch

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

The effect of hydrogen and notch orientation in SENT specimens on the fracture toughness of an API 5L X70 pipeline steel

Side-grooved Charpy impact testing: Assessment of splitting and fracture properties of high-toughness plate steels

Study on Fracture Behavior and Toughening Mechanisms of Ultra-High-Strength Pipeline Steel

Effects of defect on the hydrogen embrittlement behavior of X80 pipeline steel in hydrogen-blended natural gas environments

Tensile Deformation and Fracture Behavior of API-5L X70 Line Pipe Steel

Cracking Reasons of X70 Steel Submerged Arc Weld Pipe during Guide-Bend Test

Study on Microstructure and Tensile Behavior of X70 Dual-Phase Steel in Different Directions: Experiments and Crystal Plasticity Finite Element Method

Types and Cause of Cold Bending Crack Defects of Welded Pipe

Effect of quenching and tempering heat treatment process on microstructure and properties of X100 pipeline steel

Investigating variations in hydrogen-assisted crack propagation of X52 pipeline steel with different microstructural characteristics

Effect of through-thickness microstructure inhomogeneity on mechanical properties and strain hardening behavior in heavy-wall X70 pipeline steels

Characterization of ductile fracture criterion for API X80 pipeline steel based on a phenomenological approach

Fracture toughness tests at low temperature for thick plate in steel structures

Experimental and Theoretical Fracture Assessments of Blunt V-Notched Rock Samples Under SHPB Impact Loading

Analysis on Cracking of a Pipeline Steel Pipe during Hydraulic Burst Test

Fracture toughness assessment of the X80 steel by nanoindentation technique and a modified constitutive model

Experimental study on fracture toughness of high-strength structural steel and its butt weld

The Fatigue Crack Initiation Life of X60 Pipeline Steel after Pre-tension Deformation

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line