Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Mechanism of Delamination and Its Effects on Fracture of Surface Crack Bodies in Ductile Pipeline Steel

Effects of Thickness and Delaminating on Fracture of High Strength and High Toughness Pipeline Steel

The Delamination Crack in Ferrite Pipeline Steel and the Effect on the Fracture

Different Delamination Cracks During Fracture and Their Influences on the Fracture of X70 Pipeline Steel

Fracture Appearance Evaluation of High Performance Pipeline Steel DWTT Specimen with Delamination Cracks

Effects of Thickness and Delamination on Fracture Toughness of X60 Pipeline Steel

The Effect of Specimen Orientation and Thickness on the Initiation of Delamination Crack in X80 Pipeline Steel

Study on Fracture of Non-Through Crack Bodies of X60 Pipeline Steel

Investigation on Failure Mode of Short Carbon Fiber Reinforced Thermoplastic Composites Joints of Non-metallic Pipeline

Delamination Cracks and Fracture Evaluation in DWTT of X70 Pipeline Steel

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

FRACTURE TOUGHNESS OF X70 PIPELINE STEEL AT DIFFERENT TEMPERATURES

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

Constraint Effect on the Ductile Crack Growth Resistance of Circumferentially Cracked Pipes

Study on Fracture Behavior and Toughening Mechanisms of Ultra-High-Strength Pipeline Steel

Analysis of delaminations occurring during different rupture tests of X70 pipeline steels

The Charpy Notch Impact Test of X70 Pipeline Steel with Delamination Cracks

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

The Toughness-Induced Crack Deceleration Mechanism on Ultra-High Pressure Steel Gas Pipelines

Dynamic Ductile Fracture Toughness Test and Numerical Simulation for Ultra-High Pressure Gas Pipelines

Application of Constraint-Sensitive Fracture Mechanics to the Assessment of Girth Weld Integrity