Abstract:Silicon carbide (SiC) is an effective material for high-temperature engineering applications owing to its desirable properties such as high elastic modulus, high hardness, and melting temperature, high thermal conductivity, good corrosion and oxidation resistance, low density, and coefficient of thermal expansion compared with other advanced ceramics. Nevertheless, poor sinterability and low toughness limit its use, which can be overcome using appropriate additives. In this study, the effect of different amounts of nano-β-SiC (0, 5, 10, and 15 wt.%) and graphene (0, 1, 2, and 3 wt.%) particles on the sinterability behavior and microstructure of SiC composite has been investigated. After weighing, dispersing nano-β-SiC and graphene, and mixing the starting materials, milling was carried out at 180 rpm for 3 h. The materials obtained were then compressed uniaxially under a pressure of 75 MPa and then were compressed again through CIP under 150 MPa. To remove volatile products, the pyrolysis process was performed at 800 °C under Ar atmosphere. Finally, the samples were sintered at 2200 °C for 2 h by the pressureless sintering process. XRD analysis was used to investigate the phases and FESEM images were used to study the microstructure. According to the XRD patterns, β-SiC particles were converted to α-SiC, which was accompanied by the elongation of SiC grains. Also, no reaction was observed between graphene and the SiC matrix. According to the FESEM images, the samples containing 5 wt.% nano-β-SiC and 1 wt.% graphene showed a uniform distribution of reinforcement particles but with increasing the amount of the reinforcement particles, agglomeration was observed. According to the results, upon increasing the nano-β-SiC up to 5 wt% and graphene up to 1 wt.%, all the measured properties including relative density, and linear shrinkage improved and reached 99.04%, and 18.01%, respectively. However, with increasing the additives, these properties deteriorated due to increasing porosity and agglomeration in the composite structure.

β-SiC nano-particles enhanced thermal conductivity of pressureless solid-phase sintering SiC

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Low temperature Pr 3 Si 2 C 2 ‐assisted liquid phase sintering of SiC with improved thermal conductivity

High Thermal Conductivity in Pressureless Densified SiC Ceramics with Ultra-Low Contents of Additives Derived from Novel Boron–carbon Sources

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Thermal management applied laminar composites with SiC nanowires enhanced interface bonding strength and thermal conductivity

Improving thermal conductivity of Al/SiC composites by post-oxidization of reaction-bonded silicon carbide preforms

Preferentially oriented SiC/graphene composites for enhanced mechanical and thermal properties

Achieving Significant Thermal Conductivity Enhancement via an Ice-Templated and Sintered BN-SiC Skeleton

Pressureless sintering of SiC matrix composites reinforced with nano-β-SiC and graphene

Sintering of β-Si_3N_4 Powder and Thermal Conductivity of the Ceramic

Fluoride doped SiC/Si3N4 composite as a high thermal conductive material with enhanced mechanical properties

Study on the Performance for Silicon Carbide Ceramics by Hot-pressing Sintering

Preparation and characterization of lightweight SiC frameworks by connecting SiC fibers with SiC joints

Enhancement of thermal shock resistance in β-Si3N4 coating with in situ synthesized β-Si3N4 nanowires/nanobelts on porous Si3N4 ceramics

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

Coating dense Silicon Carbide layer on artificial graphites to achieve synergistically enhanced thermal conductivity and electronic insulation of polymer composites

Fabricating superior thermal conductivity SiC–AlN composites from photovoltaic silicon waste

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles