Abstract:The scratch test has been used to assess the adhesion of thin hard coatings for some time now and is a useful tool for coating development or quality assurance. However, the test is influenced by a number of intrinsic and extrinsic factors which are not adhesion-related and the results of the test are usually regarded as only semi-quantitative. The stress state around a moving indenter scratching a coating/substrate system is very complex and it is difficult to determine the stresses which lead to detachment. Furthermore, the interfacial defect state responsible for failure is unknown. However, by a careful analysis of the observed failure modes in the scratch test (not all of which are related to adhesion) it is possible to identify adhesive failures and in some cases these occur in regions where the stress state is relatively simple and quantification can be attempted.Ideally engineers would like a material parameter (such as work of adhesion or interfacial toughness) which can be used in an appropriate model of the coating-substrate system stress state to determine if detachment will occur under the loading conditions experienced in service. This data is not usually available and the development of such models must be seen as a long-term goal. In modern indentation and scratch systems the work of friction (or indentation) can be directly measured and the relationship between this parameter and adhesive failure can be demonstrated in some cases. This paper reviews the main adhesion-related failure modes and the stresses responsible for them and indicates where quantification is possible illustrating this with results from hard coatings on steel, thermally grown oxide scales and optical coatings on glass. The use of empirical calibration studies, directly measured work of friction and quantification by finite element methods is discussed.

Quantitative Evaluation of Bonding Strength for Hard Coatings by Interfacial Fatigue Strength under Cyclic Indentation

The Repeated Spherical Indentation Test: an Efficient Way to Evaluate the Adhesion of Hard Coatings

Evaluation of the Bond Strength of Hard Coatings by the Contact Fatigue Test

Interfacial fatigue limit as measure of cyclic bonding strength of hard coatings

Depth-Sensing Indentation-Based Studies of Surface Mechanical Behavior and Fatigue Damage Evolution of an Austenitic Stainless Steel Subjected to Cyclic Straining

An overview of the potential of quantitative coating adhesion measurement by scratch testing

Evaluation of Bonding Strength of Thin Hard Films by Spherical Rolling Test

Bonding Strengths of Pcvd Films under Cyclic Loading

An Evaluation of the Adhesive Strength of the Interface between a Coating and Substrate

Quantitative Evaluation of Adhesion of Metallic Coatings with an Extended Microbridge Test

Finite element analysis of the critical ratio of coating thickness to indentation depth for coating property measurements by nanoindentation

Approaches to Investigate Delamination and Interfacial Toughness in Coated Systems: an Overview

Measuring Interface Fracture Resistance in Thin Hard Films

The Interface Failure Criterion of Coating Materials

Assessment of the Adhesion of Ceramic Coatings

A New Method Based on Work-Displacement Curve to Assess the Toughness of Coated System

Indentation-based Methods to Assess Fracture Toughness for Thin Coatings

Novel method for measuring surface residual stress using flat-ended cylindrical indentation

A novel method to extract the equi-biaxial residual stress and mechanical properties of metal materials by continuous spherical indentation test

Internal Stress on Adhesion of Hard Coatings Synthesized by Multi-Arc Ion Plating

Finite Element Analysis of the Nanomechanics of Hard Coatings on a Soft Polymer Substrate by a Spherical Indenter