Quantitative characterization and analysis of creep constraint induced by specimen thicknesses in compact tension specimens

Pengjuan Sun,Guozhen Wang,Fu-Zhen Xuan,Shan-Tung Tu,Zhengdong Wang

2010-01-01

Abstract:In this paper, the C (t) and C* integrals for characterizing the amplitudes of. creep crack-tip stress fields, the time for stress redistribution from initial to steady-state creep conditions, t red, and creep crack-tip stress distributions in the compact tension (CT) specimens with various thicknesses have been calculated by the three-dimensional (3D) finite element method, and the creep crack-tip constraint induced by specimen thicknesses has been quantitatively characterized and analyzed. The new constraint parameter R, which is defined as the difference between 3D creep stress field and high constraint stress state under plane strain conditions was utilized. The results show that the 3D creep constraint in CT specimens could be characterized by the new constraint parameter R. The creep constraint in 3D specimen lies between the two limit cases of the plane strain and plane stress state. The creep crack-tip constraint induced by specimen thicknesses increases with increasing specimen thickness, and the crack-tip constraint levels at the regions near the mid-section in the specimens with B >= 12.5mm could be regarded as to reach that of plane strain. The 3D constraint effect becomes more pronounced with increasing the load level C. At steady state creep stage, the creep constraint in specimens with small thickness decreases with increasing load level (C), and it almost does not change with the C* for the specimens with large thickness. The 3D creep constraint at non-steady state creep is more significant than that at steady state creep. With increasing the distance from free surface to mid-section along the crack fronts, the creep constraint in 3D specimens increases. There is a central region with higher creep constraint along the crack front in the specimen, and the size of the region increases with increasing specimen thickness, and decreases with increasing creep time. The effects of creep time, load levels and distances from the crack tips on the 3D creep constraint are also analyzed.