Interface Behavior of Brazed Joints of AZ31 Magnesium Alloy Using Silver-Base Alloy Interlayer

Yang Tuoyu,Wang Kehong,Zhang Deku,Huang Jun

2017-01-01

Rare Metal Materials and Engineering

Abstract:Contact-reaction brazing was used to bond AZ31 joints in order to improve the microstructure and wettability of AZ31 magnesium alloy brazed joints. This was achieved by an AgCuZn interlayer during the brazing process without the use of a flux. The results show that a defect-free brazed joint can be obtained when the AgCuZn interlayer is completely dissolved at 500 degrees C for 15 min. The microstructure of the brazing seam consists of multiple eutectic structures. The second phase is granular and short rod-like. Both the granular and the short rod-like structures are uniformly distributed in the continuous matrix. A small amount of primary crystal taking on cloud state is present in the brazing seam center. X-ray diffraction and energy spectrum analysis indicate that the second phase consists of an alpha-Mg solid solution containing large amounts of Ag, Cu, and Zn, while the basal body consists of an AgMg3 compound and small amounts of CuMgZn compound. The mean shear strength of the brazed joints is about 108.9 MPa. Both sugar granules and cleavage steps are clearly observed in the tensile shear fracture morphologies with mixed fracture characteristics in both intergranular fractures and transgranular fractures. The AgCuZn-base interlayer influences the microstructure and mechanical properties of the brazed joints.