Effect of Welding Conditions on Microstructure and Mechanical Properties of Friction Stir Welded AZ31 Mg Alloy Joints
Lin Zhang,Zanyang Zhang,Lele Huang,Lihong Wu,Yufeng Sun,Shaokang Guan
DOI: https://doi.org/10.1007/s11837-023-05833-3
2023-04-24
JOM
Abstract:Friction stir welded (FSWed) AZ31 Mg alloy joints were prepared at two different rotation speeds, namely, 150 rpm and 500 rpm, and are referred to as FSW-150 and FSW-500, respectively. The microstructure of the FSW joints was characterized and the local strain evolution in the tensile tests was monitored by a high-resolution digital image correlation method. The results show that the stir zone (SZ) of both FSW joints showed an equiaxed grain structure and the thermal-mechanically affected zone (TMAZ) had a gradually varied texture in FSW-150, compared with the relatively stable texture in FSW-500. A basin-shaped SZ was formed in FSW-150, while a cylindrical-shaped SZ was formed in FSW-500. Due to the different shape of SZ, the strain was gradually increased in TMAZ through the thickness of the FSW-500 specimen in tensile tests. However, the FSW-150 specimen showed an inhomogeneous strain distribution through the thickness, which resulted in the shear tensile stress to be localized at the TMAZ/SZ boundary and early fracture of the tensile specimen. Finally, the FSW-500 specimen showed an improved tensile strength and elongation of 250 MPa and 17%, compared with the 210 MPa and 6% for the FSW-150 counterpart.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy