Abstract:In this work, FSW was used to join AZ31 and AZ91 magnesium (Mg) alloys to investigate the mechanism behind joint formation and its mechanical performance. The cross-sectional microstructure of the weld zone clearly indicated a strong metallurgical bonding between AZ31 and AZ91 sheets in addition to the mechanical interlocking due to the mixing of both base materials. Uniform hardness (62.9 ± 4.5 HV) was recorded in the weld joint and the values were between AZ31 (59.8 ± 2.4 HV) and AZ91 (78.7 ± 19.5 HV). Tensile test results demonstrated decreased strength (145 ± 4.2 MPa) compared with the base alloys (265 ± 7.3 MPa and 190 ± 4.8 MPa for AZ31 and AZ91, respectively. Ductility was noticed as decreased as reflected by the lower % of elongation for the weld joint compared with both AZ31 and AZ91 base materials. The fractography studies of the samples suggest a brittle mode of fracture in the weld joint similar to that of AZ91 base material. Dans ce travail, on a utilisé FSW pour assembler les alliages de magnésium (Mg) AZ31 et AZ91 dans le but d'étudier le mécanisme à l'origine de la formation du joint et ses performances mécaniques. La microstructure de la section transversale de la zone de soudure a clairement indiqué une liaison métallurgique forte entre les tôles de AZ31 et AZ91 en plus de l'enclenchement mécanique en raison du mélange des deux matériaux de base. Les composés intermétalliques étaient considérablement réduits dans la zone du noyau ainsi que l'effet d'affinement des grains. On a enregistré une dureté relativement uniforme (62.9 ± 4.5 HV) dans le joint de soudure et les valeurs se situaient entre AZ31 (59.8 ± 2.4 HV) et AZ91 (78.7 ± 19.5 HV). Les résultats d'essai de traction ont présenté une résistance réduite (145 ± 4.2 MPa) par rapport aux alliages de base (265 ± 7.3 MPa et 190 ± 4.8 MPa pour AZ31 et AZ91, respectivement). On a noté que la ductilité avait diminué, comme le reflète le pourcentage d'élongation plus faible du joint soudé par rapport aux matériaux de base, AZ31 et AZ91. Les études fractographiques des échantillons suggèrent un mode de rupture fragile dans le joint de soudure similaire à celui du matériau de base AZ91.

Effect of Microstructure and Microtexture on Mechanical Properties and Fracture Behaviour of Friction Stir-Welded AZ31/AZ61 Joint

Improving the mechanical properties of a friction stir welded AZ31 joint by adjusting the microstructure and texture

Improving microstructural and mechanical properties of dissimilar friction stir welded AZ61/AZ40 joint

Influence of Friction Stir Welding on Mechanical Properties of Butt Joints of AZ61 Magnesium Alloy

Characteristics of Microstructure and Microhardness of Friction Stir Welded Joints for AZ31 Magnesium Alloy

Effect of Low Welding and Rotational Speed on Microstructure and Mechanical Behaviour of Friction Stir Welded AZ31-AA6061-T6

Microstructure and Mechanical Properties of Friction Stir-Welded Dissimilar Joints of ZK60 and Mg-4.6Al-1.2Sn-0.7Zn Alloys

Analysis of Microstructure and Mechanical Properties of AZ31B Thick Plate Magnesium Alloy Stir Friction Welded Joints

Microstructural and mechanical properties of Al–Mg–Si–Cu joint fabricated by rotary friction welding

Parametric effect on microstructure evolution, grain size and mechanical behaviour of friction stir butt welding of AA6061-T6 alloy

Effect of Tool Speed on Microstructure Evolution and Mechanical Properties of Friction Stir Welded Joints of Al-Mg-Si Alloy with High Cu Content

Microstructure and abnormal mechanical properties under the coupling effect of strain and temperature for friction-stir-welded joints of Al-Mg-Si alloy

Effect of welding speed on microstructure and mechanical properties of Al−Mg−Mn−Zr−Tialloy sheet during friction stir welding

Microstructure and Mechanical Property Improvement of AZ31B Induced by the Combination of Cold Metal Transfer Welding and Friction Stir Processing

Effect of Welding Conditions on Weld Zone Temperature and Mechanical Properties of Friction Stir Welded AZ61 Magnesium Alloy Sheet

Enhanced mechanical properties of thermo-mechanically affected zone of friction-stir welded AZ61 magnesium alloy joint

Influences of welding parameters on mechanical properties of AZ31 friction stir spot welds

Microstructure evolution of thermo-mechanically affected zone in dissimilar AA2024/7075 joint produced by friction stir welding

Clarification of microstructure and texture evolution of friction stir–welded dissimilar AA7075/AZ31B using ultrasonic assistance

Investigating the weld joint characteristics of AZ31 and AZ91 magnesium alloys produced by friction stir welding

Microstructural characterization and mechanical properties of inertia friction welded FGH96 joints