Abstract:In the present work, a novel Ni-Cu composite interlayer was prepared on the surface of A356 aluminum alloy solid insert using the chemical nickel-plating and electro-coppering technology, in order to restrain the generation of brittle phases and enhance the shear strength of A356 aluminum/AZ91D magnesium bimetal manufactured using a compound casting. The effect of the Ni-Cu composite interlayer on the microstructure, mechanical properties and corrosion resistance of the bimetal was studied. The results show that the Ni-Cu composite interlayer effectively restrained the generation of the brittle and hard Al-Mg intermetallic compounds (IMCs). The interface layer of the A356/AZ91D bimetal without Ni-Cu composite interlayer was composed of Al3Mg2, Al12Mg17, δ-Mg and Mg2Si phases, while the interfacial reactants of the A356/AZ91D bimetal with Ni-Cu composite interlayer were mainly Al3Ni, Ni (Cu), Cu (Ni), Mg2Cu and Al7Cu3Mg6 phases. With the application of the Ni-Cu composite interlayer, the thickness of the interface of the A356/AZ91D bimetal remarkably decreased from 1400 μm of the sample without Ni-Cu composite interlayer to 40 μm. The shear strength of the A356/AZ91D bimetal using Ni-Cu composite interlayer increased by 20.3% compared with that of the bimetal without Ni-Cu composite interlayer. The fractures of the A356/AZ91D bimetals with and without Ni-Cu composite interlayers belonged to a brittle rupture mode. The breakage of the bimetal with Ni-Cu composite interlayer mainly took place between the Ni-Cu layer and AZ91D matrix, while the rupture of the A356/AZ91D bimetal without Ni-Cu composite interlayer was located in the interface layer. The Cu(Ni) and Ni(Cu) layers had a lower nano-hardness than the Al-Mg IMCs, and the elasticity modulus for the Cu(Ni), Ni(Cu) and Al3Ni phases were higher compared to those of the Al-Mg IMCs. The results of corrosion test exhibited that the Ni-Cu composite interlayer had little influence on the corrosion resistance of the A356/AZ91D bimetal.

The Effect of a Zinc Interlayer on the Microstructure and Mechanical Properties of a Magnesium Alloy (AZ31)–Aluminum Alloy (6060) Joint Produced by Liquid–Solid Compound Casting

Joining mechanism, microstructure, and mechanical properties of AZ31/6061 joint prepared by pouring fusion welding process assisted with Zn-xSn brazing filler

Interfacial structure of the joints between magnesium alloy and mild steel with nickel as interlayer

Influence of the Zn interlayer on the mechanical strength, corrosion and microstructural behavior of friction stir-welded 6061-T6 aluminium alloy and AZ61 magnesium alloy dissimilar joints

An investigation on diffusion bonding of Mg/Al dissimilar metals using Zn-Bi alloy as interlayer

Joining Mg Alloys with Zn Interlayer by Novel Ultrasonic-Assisted Transient Liquid Phase Bonding Method in Air

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Zn-brazed-interface on Microstructures and Mechanical Properties of Dissimilar 2A12/AZ31 Alloys Friction Stir Lap Welds

Effect of vertical and horizontal zinc interlayer on material flow, microstructure, and mechanical properties of dissimilar FSW of Al 7075 and Mg AZ31 alloys

Interface Behavior of Brazed Joints of AZ31 Magnesium Alloy Using Silver-Base Alloy Interlayer

Effect of a Zn interlayer on the formation mechanism and mechanical performance of AA6061/DP590 steel resistance riveting welding

Effects of Al/Zn interlayer on the solidification path and liquation cracking susceptibility of AZ31/ZK61 dissimilar magnesium alloy resistance spot welding joints

Microstructure, mechanical properties and corrosion resistance of A356 aluminum/AZ91D magnesium bimetal prepared by a compound casting combined with a novel Ni-Cu composite interlayer

Effects of Zr interlayer on microstructure, mechanical property and corrosion behavior of Al/Mg dissimilar friction stir welding lap joints

Effects of Zn Interlayer on Microstructures and Mechanical Properties of TC4/AZ91D Bimetal via Solid–Liquid Compound Casting Process

Analysis of Microstructure and Mechanical Properties of AZ31B Magnesium Alloy/AA6061 Aluminum Alloy Welded Joint by Ultrasonic Welding

Improved mechanical and corrosion properties of friction stir welded Al/Mg dissimilar lap joints by Zr interlayer addition

Joint formation and mechanical properties of ultrasonic-assisted transient liquid bonding of dissimilar Al/Mg with a Zn interlayer in air

Improving mechanical properties of AZ91D magnesium/A356 aluminum bimetal prepared by compound casting via a high velocity oxygen fuel sprayed Ni coating

Microstructure and Mechanical Properties of AZ31B/LY12 Joints Using Zn/Ag–Cu–Zn/Zn Multi-Interlayers via Ultrasound-Assisted Transient Liquid Phase Bonding

Microstructural characterization and mechanical behavior of Mg-AZ31B/Al 6063 bimetallic sheets produced by combining continuous shear deformation with direct extrusion