Abstract:In the present work, a novel Ni-Cu composite interlayer was prepared on the surface of A356 aluminum alloy solid insert using the chemical nickel-plating and electro-coppering technology, in order to restrain the generation of brittle phases and enhance the shear strength of A356 aluminum/AZ91D magnesium bimetal manufactured using a compound casting. The effect of the Ni-Cu composite interlayer on the microstructure, mechanical properties and corrosion resistance of the bimetal was studied. The results show that the Ni-Cu composite interlayer effectively restrained the generation of the brittle and hard Al-Mg intermetallic compounds (IMCs). The interface layer of the A356/AZ91D bimetal without Ni-Cu composite interlayer was composed of Al3Mg2, Al12Mg17, δ-Mg and Mg2Si phases, while the interfacial reactants of the A356/AZ91D bimetal with Ni-Cu composite interlayer were mainly Al3Ni, Ni (Cu), Cu (Ni), Mg2Cu and Al7Cu3Mg6 phases. With the application of the Ni-Cu composite interlayer, the thickness of the interface of the A356/AZ91D bimetal remarkably decreased from 1400 μm of the sample without Ni-Cu composite interlayer to 40 μm. The shear strength of the A356/AZ91D bimetal using Ni-Cu composite interlayer increased by 20.3% compared with that of the bimetal without Ni-Cu composite interlayer. The fractures of the A356/AZ91D bimetals with and without Ni-Cu composite interlayers belonged to a brittle rupture mode. The breakage of the bimetal with Ni-Cu composite interlayer mainly took place between the Ni-Cu layer and AZ91D matrix, while the rupture of the A356/AZ91D bimetal without Ni-Cu composite interlayer was located in the interface layer. The Cu(Ni) and Ni(Cu) layers had a lower nano-hardness than the Al-Mg IMCs, and the elasticity modulus for the Cu(Ni), Ni(Cu) and Al3Ni phases were higher compared to those of the Al-Mg IMCs. The results of corrosion test exhibited that the Ni-Cu composite interlayer had little influence on the corrosion resistance of the A356/AZ91D bimetal.

Effects of Zn Interlayer on Microstructures and Mechanical Properties of TC4/AZ91D Bimetal via Solid–Liquid Compound Casting Process

Investigation of Cu Interlayer on Joint Formation of Ti/Mg Bimetal Fabricated by Liquid–Solid Compound Casting Process

Influence of Ni‐Coating Thickness on Interface Microstructure and Mechanical Properties of Mg/Ti Bimetal via Compound Casting

Interface Microstructure Regulation of Mg/Ti Bimetals by Thermal Diffusion Treatment of Ni-coated TC4 Alloy

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effect of Multi-component Alloy Interlayer on Interfacial Microstructure and Shear Strength of Titanium/Bronze Bimetal

Impacts of Zinc Layer and Pouring Method on Interface Performance for Al-22Si/ZL104 Bi-Metal

Microstructure evolution of the Zr-4 alloy joints diffusion bonded with pure titanium interlayer and its influence on joint properties

The Effect of a Zinc Interlayer on the Microstructure and Mechanical Properties of a Magnesium Alloy (AZ31)–Aluminum Alloy (6060) Joint Produced by Liquid–Solid Compound Casting

Effect of Al22Si/ZL102 Bimetal Interface Fabricated by Extrusion at Neareutectic Temperature

Microstructure, mechanical properties and corrosion resistance of A356 aluminum/AZ91D magnesium bimetal prepared by a compound casting combined with a novel Ni-Cu composite interlayer

The Solidification and Corrosion Behavior Determination of the Ti/B Added Zn-Al-Mg Alloys

Effects of Zr?based Amorphous Alloy Interlayer on Microstructure and Properties of Al/TA1 Dissimilar Metals Electron Beam Welded Joints

Improving mechanical properties of AZ91D magnesium/A356 aluminum bimetal prepared by compound casting via a high velocity oxygen fuel sprayed Ni coating

The Effect of Zr and Li on the Microstructure of AlMg5Si2Mn-Type Casting Alloys

The Effect of the Cu Interlayer on the Interfacial Microstructure and Mechanical Properties of Al/Fe Bimetal by Compound Casting

The pre-hot dipping effects on the bimetal casting of nitriding steel sleeve into the Al-Si matrix

Optimization of the Microstructure and Mechanical Properties of a TC4 Alloy Joint Brazed with a Zr-Based Filler Containing a Co Element

Study on the Microstructure of Mg-4Zn-4Sn-1Mn-xAl As-Cast Alloys

Interfacial characteristics and bending properties of a Ti6Al4V-Mg3AlZn laminate metal composite