Abstract:Highlights • Microstructure and mechanical behavior of Al-xSi/AZ91D bimetallic composites were studied. • Thickness of interface of Al/Mg bimetallic composites decreased with increasing Si content. • Oxide inclusion defects in interface layer decreased with increasing Si content. • Increasing Si content resulted in an inconsistent preferred orientation of interface layer. • Shear strength of the composites increased with increasing Si content, obtaining a maximum value with 15 wt.% Si. In this paper, the effect of the Si content on microstructure evolution, mechanical properties, and fracture behavior of the Al-xSi/AZ91D bimetallic composites prepared by compound casting was investigated systematically. The obtained results showed that all the Al-xSi/AZ91D bimetallic composites had a metallurgical reaction layer (MRL), whose thickness increased with increasing Si content for the hypoeutectic Al-Si/AZ91D composites, while the hypereutectic Al-Si/AZ91D composites were opposite. The MRL included eutectic layer (E layer), intermetallic compound layer (IMC layer) and transition region layer (T layer). In the IMC layer, the hypereutectic Al-Si/AZ91D composites contained some Si solid solution and flocculent Mg 2 Si+Al-Mg IMCs phases not presented in the hypoeutectic Al-Si/AZ91D composites. Besides, increasing Si content, the thickness proportion of the T layer increased, forming an inconsistent preferred orientation of the MRL. The shear strengths of the Al-xSi/AZ91D bimetallic composites enhanced with increasing Si content, and the Al-15Si/AZ91D composite obtained a maximum shear strength of 58.6 MPa, which was 73.4% higher than the Al-6Si/AZ91D composite. The fractures of the Al-xSi/AZ91D bimetallic composites transformed from the T layer into the E layer with the increase of the Si content. The improvement of the shear strength of the Al-xSi/AZ91D bimetallic composites was attributed to the synergistic action of the Mg 2 Si particle reinforcement, the reduction of oxidizing inclusions and the ratio of Al-Mg IMCs as well as the orientation change of the MRL.

Effect of Al22Si/ZL102 Bimetal Interface Fabricated by Extrusion at Neareutectic Temperature

Study on interface behavior of Be/CuCrZr alloy by diffusion bonding

Impacts of Zinc Layer and Pouring Method on Interface Performance for Al-22Si/ZL104 Bi-Metal

Evolution of interfacial structure and fracture behavior in ZL702A/SUS304 compound castings with different surface treatments

Effects of Zn Interlayer on Microstructures and Mechanical Properties of TC4/AZ91D Bimetal via Solid–Liquid Compound Casting Process

Interface Behaviors and Mechanical Properties of Diffusion Bonded 45 Steel/additive Manufactured 316L Steel Joints

Effect of Zn-brazed-interface on Microstructures and Mechanical Properties of Dissimilar 2A12/AZ31 Alloys Friction Stir Lap Welds

An Investigation into Aluminum–aluminum Bimetal Fabrication by Squeeze Casting

Strengthening of compound casting Al/Mg bimetallic interface with Ni interlayer by vibration assisted treatment

The Effect of the Cu Interlayer on the Interfacial Microstructure and Mechanical Properties of Al/Fe Bimetal by Compound Casting

An Investigation into Interface Formation and Mechanical Properties of Aluminum–copper Bimetal by Squeeze Casting

Microstructural characterization and mechanical behavior of Mg-AZ31B/Al 6063 bimetallic sheets produced by combining continuous shear deformation with direct extrusion

Fabrication and Interface Structural Behavior of Mg/Al Thickness-Oriented Bonding Sheet via Direct Extrusion

Achieving Metallurgical Bonding in Aluminum/Steel Bimetallic Castings

Microstructure and age hardening behavior of Al/Fe bimetal prepared by one-step compound casting

Interfacial Microstructure and Mechanical Properties of Al/steel Joints Fabricated Via Thermo-Compensated Resistance Brazing Welding with Cold Spray Zn Interlayer

Effect of Multi-component Alloy Interlayer on Interfacial Microstructure and Shear Strength of Titanium/Bronze Bimetal

Microstructure evolution, mechanical properties and fracture behavior of Al-xSi/AZ91D bimetallic composites prepared by a compound casting

Effect of Zn/Mg ratio on the microstructure and properties of Al-xZn-2.0Mg-1.0Cu-0.2Zr-yTi ultrahigh-strength aluminum alloy extrusion

Effect of high entropy alloy as the interlayer on the interfacial microstructure and mechanical property of Al/steel bimetal by compound casting

The pre-hot dipping effects on the bimetal casting of nitriding steel sleeve into the Al-Si matrix