Microstructure, mechanical properties and corrosion resistance of A356 aluminum/AZ91D magnesium bimetal prepared by a compound casting combined with a novel Ni-Cu composite interlayer
Guangyu Li,Wenming Jiang,Feng Guan,Junwen Zhu,Zheng Zhang,Zitian Fan
DOI: https://doi.org/10.1016/j.jmatprotec.2020.116874
IF: 6.3
2021-02-01
Journal of Materials Processing Technology
Abstract:<p>In the present work, a novel Ni-Cu composite interlayer was prepared on the surface of A356 aluminum alloy solid insert using the chemical nickel-plating and electro-coppering technology, in order to restrain the generation of brittle phases and enhance the shear strength of A356 aluminum/AZ91D magnesium bimetal manufactured using a compound casting. The effect of the Ni-Cu composite interlayer on the microstructure, mechanical properties and corrosion resistance of the bimetal was studied. The results show that the Ni-Cu composite interlayer effectively restrained the generation of the brittle and hard Al-Mg intermetallic compounds (IMCs). The interface layer of the A356/AZ91D bimetal without Ni-Cu composite interlayer was composed of Al<sub>3</sub>Mg<sub>2</sub>, Al<sub>12</sub>Mg<sub>17</sub>, δ-Mg and Mg<sub>2</sub>Si phases, while the interfacial reactants of the A356/AZ91D bimetal with Ni-Cu composite interlayer were mainly Al<sub>3</sub>Ni, Ni (Cu), Cu (Ni), Mg<sub>2</sub>Cu and Al<sub>7</sub>Cu<sub>3</sub>Mg<sub>6</sub> phases. With the application of the Ni-Cu composite interlayer, the thickness of the interface of the A356/AZ91D bimetal remarkably decreased from 1400 μm of the sample without Ni-Cu composite interlayer to 40 μm. The shear strength of the A356/AZ91D bimetal using Ni-Cu composite interlayer increased by 20.3% compared with that of the bimetal without Ni-Cu composite interlayer. The fractures of the A356/AZ91D bimetals with and without Ni-Cu composite interlayers belonged to a brittle rupture mode. The breakage of the bimetal with Ni-Cu composite interlayer mainly took place between the Ni-Cu layer and AZ91D matrix, while the rupture of the A356/AZ91D bimetal without Ni-Cu composite interlayer was located in the interface layer. The Cu(Ni) and Ni(Cu) layers had a lower nano-hardness than the Al-Mg IMCs, and the elasticity modulus for the Cu(Ni), Ni(Cu) and Al<sub>3</sub>Ni phases were higher compared to those of the Al-Mg IMCs. The results of corrosion test exhibited that the Ni-Cu composite interlayer had little influence on the corrosion resistance of the A356/AZ91D bimetal.</p>
materials science, multidisciplinary,engineering, manufacturing, industrial