Abstract:In the present work, a novel Ni-Cu composite interlayer was prepared on the surface of A356 aluminum alloy solid insert using the chemical nickel-plating and electro-coppering technology, in order to restrain the generation of brittle phases and enhance the shear strength of A356 aluminum/AZ91D magnesium bimetal manufactured using a compound casting. The effect of the Ni-Cu composite interlayer on the microstructure, mechanical properties and corrosion resistance of the bimetal was studied. The results show that the Ni-Cu composite interlayer effectively restrained the generation of the brittle and hard Al-Mg intermetallic compounds (IMCs). The interface layer of the A356/AZ91D bimetal without Ni-Cu composite interlayer was composed of Al3Mg2, Al12Mg17, δ-Mg and Mg2Si phases, while the interfacial reactants of the A356/AZ91D bimetal with Ni-Cu composite interlayer were mainly Al3Ni, Ni (Cu), Cu (Ni), Mg2Cu and Al7Cu3Mg6 phases. With the application of the Ni-Cu composite interlayer, the thickness of the interface of the A356/AZ91D bimetal remarkably decreased from 1400 μm of the sample without Ni-Cu composite interlayer to 40 μm. The shear strength of the A356/AZ91D bimetal using Ni-Cu composite interlayer increased by 20.3% compared with that of the bimetal without Ni-Cu composite interlayer. The fractures of the A356/AZ91D bimetals with and without Ni-Cu composite interlayers belonged to a brittle rupture mode. The breakage of the bimetal with Ni-Cu composite interlayer mainly took place between the Ni-Cu layer and AZ91D matrix, while the rupture of the A356/AZ91D bimetal without Ni-Cu composite interlayer was located in the interface layer. The Cu(Ni) and Ni(Cu) layers had a lower nano-hardness than the Al-Mg IMCs, and the elasticity modulus for the Cu(Ni), Ni(Cu) and Al3Ni phases were higher compared to those of the Al-Mg IMCs. The results of corrosion test exhibited that the Ni-Cu composite interlayer had little influence on the corrosion resistance of the A356/AZ91D bimetal.

An Al–7Si Alloy/cast Iron Bimetallic Composite with Super-High Shear Strength

High-Resolution Electron Microscope Observation of Interface Microstructure of A Cast Al-Mg-Si-Bi-Pb(6262)/Al2o3p Composite

The Effect of the Cu Interlayer on the Interfacial Microstructure and Mechanical Properties of Al/Fe Bimetal by Compound Casting

Evolution of interfacial structure and fracture behavior in ZL702A/SUS304 compound castings with different surface treatments

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Effect of high entropy alloy as the interlayer on the interfacial microstructure and mechanical property of Al/steel bimetal by compound casting

Microstructure, mechanical properties and corrosion resistance of A356 aluminum/AZ91D magnesium bimetal prepared by a compound casting combined with a novel Ni-Cu composite interlayer

Microstructure and age hardening behavior of Al/Fe bimetal prepared by one-step compound casting

Enhanced strength and ductility of high chromium cast iron/low carbon steel bimetal by heterostructure design

Microstructural and mechanical characterization of Al/Cu interface in a bimetallic composite produced by compound casting

Optimization of insert roughness and pouring conditions to maximize bond strength of (Cp)Al-SS304 bimetallic castings using RSM-GA coupled technique

Superior bonding of Al/Mg interface by introducing nanocrystals via high-entropy alloy coating and ultrasonic vibration

Enhanced strength-ductility synergy of Al/Zn/Al laminated composite with unique interface and multi-modal heterogeneous microstructure

Combined effects of ultrasonic vibration and FeCoNiCrCu coating on interfacial microstructure and mechanical properties of Al/Mg bimetal by compound casting

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Enhanced bonding strength of Al/Fe bimetal by Ni-based alloys Ni-based interlayer prepared by laser cladding technique

Strengthening of compound casting Al/Mg bimetallic interface with Ni interlayer by vibration assisted treatment

Significantly improved bonding strength of Al/Mg bimetallic interface by compound casting via FeCoNiCrCu high entropy alloy coating

Reinforcing Al matrix composites by novel intermetallic/SiC interface and transition structure

Super Bonding Strength of Al2O3 Nanoparticles Reinforced Sn Interlayer Steel/Aluminum Bimetal Casting

Impacts of Zinc Layer and Pouring Method on Interface Performance for Al-22Si/ZL104 Bi-Metal