Friction stir welding between the high-pressure die casting of AZ91 magnesium alloy and A383 aluminum alloy

Peiqi Li,Guoqiang You,Hengyu Wen,Wei Guo,Xin Tong,Sha Li
DOI: https://doi.org/10.1016/j.jmatprotec.2018.08.044
IF: 6.3
2019-02-01
Journal of Materials Processing Technology
Abstract:Defect-free Friction stir welded joints between the AZ91 Mg alloy and A383 Al alloy were obtained at a welding speed of 40 mm/min and a rotational speed of 900 rpm. Mg and Al were intermixed and presented intercalated strips microstructure. The second phases Si, Al3Mg2, Al12Mg17 and Mg2Si distributed uniformly in stir zone at a rotational speed of 900 rpm, and there is a narrow intermetallic compounds layer (∼10 μm) at the interface of the two base metals. The tensile strength of the dissimilar AZ91/A383 joint is 93 MPa, which is approximately 45% of the A383 alloy. The sufficient material intermixing and uniform distribution of second phases are helpful to the joint properties.
materials science, multidisciplinary,engineering, manufacturing, industrial
What problem does this paper attempt to address?