Abstract:Dissimilar friction stir welding (FSW) of ZK60 and AZ31 magnesium alloys was studied. Two kinds of material arrangements, with ZK60 or AZ31 in advancing side (AS), were applied. The results showed that the dissimilar plates with both material arrangements were joined successfully. No obvious defect was observed. Microstructure and texture variation across the joints were examined by scanning electron microscope (SEM) and electron backscatter diffraction (EBSD). The grains in stir zone (SZ) were significantly refined during FSW (∼8.7μm in AZ31 side and ∼2.7μm in ZK60 side). The second phases in ZK60 side were broken up, which contributed to grain refinement. Two-dimensional (2D) hardness maps across the normal direction (ND)—transverse direction (TD) sections in the joints were obtained. Clear boundary was observed between SZ and AZ31 base metal, but it was less clear between SZ and ZK60 base metal. The mixture of materials, grain refinement and broken up of particles were responsible for the sharp increasing of hardness between SZ and AZ31 base metal. The transverse ultimate tensile strength (UTS) of the joints was 78–82% of AZ31 base metal. The joints consistently fractured in the transition region of the AZ31 side. The sudden hardness decrease from SZ to AZ31 base metal might result in deformation incompatibility at the interface, which is considered as the main cause for the failing in the AZ31 side. In addition, the activation of twinning in SZ-side (with c-axis parallel to TD) and slip in the region adjacent to the SZ-side (with c-axis at ∼45° angle to TD) aggregated the deformation incompatibility in the transition region of the AZ31 side. As a result, the break of the specimens started at the boundary of transition zone (TZ)/SZ. Many extension twins were observed in AZ31–SZ-side after fracture. Although the ZK60–SZ-side presented the similar texture with the AZ31–SZ-side, much less extension twins were observed in the former because of the hindering effects by the refined grains and secondary particles.

Dissimilar friction stir welding of 6061 aluminum alloy and AZ31 magnesium alloy assisted with ultrasonic

Investigation of Ultrasonic Assisted Friction Stir Spot Welding of Magnesium Alloy to Aluminum Alloy

Ultrasonic Influence on Macrostructure and Mechanical Properties of Friction Stir Welded Joints of Al/Mg Sheets with 2 mm Thickness

Improving Tensile Properties of Al/Mg Joint by Smashing Intermetallic Compounds Via Ultrasonic-Assisted Stationary Shoulder Friction Stir Welding

Dissimilar Al/Mg alloys friction stir lap welding with Zn foil assisted by ultrasonic

Ultrasonic effects on microstructures and mechanical properties of friction stir weld joints of dissimilar AA2024/AZ31B alloys

Friction Stir Lap Welding of Al to Mg Assisted by Ultrasound and a Zn Interlayer

Interface Formation of Medium-Thick AA6061 Al/AZ31B Mg Dissimilar Submerged Friction Stir Welding Joints

Microstructure Evolution and Mechanical Properties of High-Speed Friction Stir Welded Aluminum Alloy Thin Plate Joints

Effect of material position and tool offset on the microstructure and mechanical properties of friction stir welded AA7075/AZ31B with ultrasonic assistance

Microstructures and Mechanical Properties of Thin Plate Aluminium Alloy Joint Prepared by High Rotational Speed Friction Stir Welding

Friction Stir Welding of AZ31B Magnesium Alloy with 6061-T6 Aluminum Alloy: Influence of Processing Parameters on Microstructure and Mechanical Properties

Microstructures and Mechanical Properties of Micro Friction Stir Welding (μfsw) of 6061-T4 Aluminum Alloy

In-situ nanocomposite in friction stir welding of 6061-T6 aluminum alloy to AZ31 magnesium alloy

Material Flow Behavior and Thermal Cycle during Friction Stir Welding of AA5083/AZ91 Dissimilar Metals

Effect of ultrasonic vibration and heat pipe assistance on microstructure and mechanical properties of friction stir-welded AZ31 alloy

Characterization of Newly Developed Friction Stir-Arc Welding Method for AM60/AZ31 Dissimilar Mg Alloy

An experimental insight of friction stir welding of dissimilar AA 6061/Mg AZ 31 B joints

Microstructure and Mechanical Properties of Friction Stir Welded Dissimilar Mg Alloys of ZK60–AZ31

Improving Joint Performance of Friction Stir Welded AZ31/ AM60 Dissimilar Mg Alloys by Double-Sided Welding

Study on the effects of ultrasonic assistance and external heat dissipation on friction stir welded 7075 aluminum alloy joints