Study on process, microstructure and mechanical properties of 6061/AZ31 dissimilar metal joining with direct contact reaction brazing

Liang Chang,Da Yu,Zhentai Zheng,Yang Zhang,Mengfei Cui,Peng Du

DOI: https://doi.org/10.1080/01694243.2024.2309844

IF: 2.431

2024-02-13

Journal of Adhesion Science and Technology

Abstract:In this study, 6061-Al and AZ31-Mg were successfully joined using the contact reaction brazing process without an interlayer under a pressure of 2 MPa and a vacuum of 1 Pa. The study examined the microstructure and mechanical properties of 6061/AZ31 joints, as well as the impact of process parameters including heating mode, cooling rate, heating temperature, and holding time on the joints. The results show that the 6061/AZ31 brazing seam can be divided into two zones: the liquid-phase solidification zone and the diffusion reaction zone. The liquid-phase solidification zone consists of the (α-Mg + Al 12 Mg 17 ) eutectic organization and precipitation phases distributed therein. The diffusion reaction zone mainly consists of the Al 3 Mg 2 layer in the brazing seam close to the 6061. Fractures in joints mainly occur in the diffusion reaction zone, where the hard and brittle Al 3 Mg 2 layer is located and extends into the liquid-phase solidification zone. Brazing joint quality was better with a cooling rate of 5 °C/s and heating without pre-weld and post-weld holding processes. The highest joint shear strength of 37 MPa was achieved at 445 °C with a holding time of 5 s. The joint exhibited no obvious defects, and the axial shrinkage of the specimen was 0.414 mm, with minimal deformation.

materials science, multidisciplinary,engineering, chemical,mechanics