Microstructure, mechanical properties and fracture behavior of GH3535 alloy joints brazed with Au-18Ni filler metal

Zhaolong Li,Haichuan Shi,Yanchun Zhao,Junjie Gu,Peilei Zhang,Zhishui Yu,Qinghua Lu,Hua Yan,Tianzhu Sun

DOI: https://doi.org/10.1016/j.jmrt.2023.09.147

IF: 6.267

2023-09-21

Journal of Materials Research and Technology

Abstract:Vacuum brazing of GH3535 alloy was conducted using Au-18Ni (wt%) filler metal. The effect of brazing temperature on the microstructure and mechanical properties was investigated. Furthermore, the microstructural evolution and fracture mechanisms of brazed joints were discussed. The cross section of brazed joint could be divided into two distinctive reaction zones. The typical microstructure of the joint brazed at 1030 °C/10min was GH3535 substrate/Ni (s.s) + Mo-rich Ni (s.s) + Au-rich phase/Au (s.s) + FeNi 3 /Au-rich phase + Mo-rich Ni (s.s) + Ni (s.s) + GH3535 substrate. Raising the brazing temperature promoted the diffusion of elements, Ni (s.s) and Au (s.s) gradually increased, and the second phase particles consisting of FeNi 3 gradually decreased. With the increase in brazing temperature, the shear strength of brazed joints first increased and then decreased. The maximum room shear strength of 420MPa was obtained at 960 °C/25min and the high temperature shear strength of 153MPa was obtained at 600°C. Fracture analysis indicated that cracks initiated at the interface of Au (s.s) and then propagated along the zone of FeNi 3 with dimple and tearing ridges patterns.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to solve the connection reliability problem of GH3535 alloy in extreme working environments such as molten - salt reactors (MSR). Specifically, the research focuses on the influence of brazing temperature on the microstructure, mechanical properties and fracture behavior when using Au - 18Ni filler metal for vacuum brazing of GH3535 alloy.

### Main problems:
1. **Improve connection reliability**: Since the GH3535 alloy works in harsh environments such as high temperature, molten - salt corrosion and neutron radiation, the reliability of its connection parts is crucial.
2. **Optimize brazing process parameters**: By studying the microstructure and mechanical properties of joints at different brazing temperatures, find the optimal brazing process parameters to ensure that the joints have good mechanical strength and durability.
3. **Understand fracture mechanism**: Analyze the fracture paths and morphologies of joints at different temperatures, and reveal their fracture mechanisms, providing a theoretical basis for further improving the brazing process.

### Research contents:
- **Microstructure evolution**: The microstructure changes of joints at different brazing temperatures were studied, including phase composition, element diffusion and distribution of second - phase particles.
- **Mechanical property evaluation**: The shear strength of joints was evaluated through room - temperature and high - temperature tensile tests, and the influence of temperature on joint performance was analyzed.
- **Fracture behavior analysis**: Through the morphological observation of fracture surfaces, the fracture mechanism of joints was explored, especially the crack initiation and propagation paths.

### Key findings:
- **Optimal brazing temperature**: Under the condition of 960°C/14°C/25min, the room - temperature shear strength of the joint reaches a maximum value of 420 MPa; at 600°C/14°C, the high - temperature shear strength is 153 MPa.
- **Fracture path**: As the brazing temperature increases, cracks mainly initiate along the Au(s.s) interface and propagate along the FeNi₃ region, showing fracture characteristics of dimples and tearing ridges.
- **Relationship between microstructure and properties**: A higher brazing temperature promotes element diffusion, reduces the number of second - phase particles, and improves the mechanical properties of joints, but may also lead to overheating embrittlement.

Through these studies, the author provides important theoretical and technical support for the application of GH3535 alloy in molten - salt reactors, which helps to improve its reliability and safety in extreme environments.