Abstract:For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications, a novel Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal was employed to join TiAl to Ni-based superalloy (GH536). The effects of brazing temperature on interfacial microstructure and chemical composition of the joints were analyzed. The representative joint microstructure from TiAl substrate to GH536 substrate was primarily composed of four characteristic layers in order: B2; Al3NiTi2; AlNi2Ti containing Cr-rich (Cr, Ni, Fe)ss (subscript ss represents solid solution), Ni-rich (Ni, Cr, Fe)ss and TiNi3; Cr-rich (Cr, Ni, Fe)ss containing AlNi2Ti, Ni-rich (Ni, Cr, Fe)ss and TiNi3. Layer IV has the majority of the brazing seam, while Layer II was the thinnest. And the thickness of Layer II was not affected by brazing temperature. With the increase in brazing temperature in the range of 1110–1170 °C, both the shear strength and the thickness of brazing seam firstly increased and then decreased. The joint performance was jointly controlled by the thickness of brazing seam, the amounts of microcracks and intermetallic compounds formed in brazing seam. The maximum shear strength of 183 MPa at room temperature was obtained together with a peak thickness when the joint was brazed at 1150 °C for 10 min and the shear fracture mainly occurred in the thinnest Layer II Al3NiTi2.<h3 class="a-plus-plus">Graphic abstract</h3>

Microstructure and shear strength of γ-TiAl/GH536 joints brazed with Ti−Zr−Cu−Ni−Fe−Co−Mo filler alloy

Microstructure evolution and mechanical properties of TiAl/GH536 joints vacuum brazed with Ti–Zr–Cu–Ni filler metal

Microstructure and mechanical properties of TiAl/Ni-based superalloy joints vacuum brazed with Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal

Microstructure and shear strength of reactive brazing joints of TiAl/Ni-based alloy

Microstructure and properties of the TiAl/GH3030 dissimilar joints vacuum-brazed with a Ti-based amorphous filler metal

Microstructure and brazing mechanism of TiAl/Ni-based superalloy joints using Ti-Zr-Cu-Ni-Co-Mo-B filler metal with different cooling rates

Interfacial features of TiAl alloy/316L stainless steel joint brazed with Zr−Cu−Ni−Al amorphous filler metal

Microstructure Evolution and Brazing Mechanism of Ti5Si3/Ti3Al Composite and Ni-based Superalloy Joints Using Ti-Zr-Cu-Ni Filler Alloy

Effect of Brazing Parameters on Microstructure and Mechanical Properties of Ti5Si3/Ti3Al Composite Joints Brazed with Ti–Zr–Cu–Ni Filler Alloy

Relationship between microstructure and mechanical properties of TiAl/Ti2AlNb joint brazed using Ti-27Co eutectic filler metal

Interfacial microstructure and properties of Ti53311S titanium alloy joints brazed using TiZrNiCu filler metal

Interfacial microstructure and properties of brazing joints of TiAl/Ni-based alloy

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Interfacial Microstructure and Mechanical Properties of TZM Alloy Joints Vacuum Brazed Using Ti-Zr-Ni-Cu Filler Metal

Vacuum brazing TiAl intermetallics to GH3030 alloy with a multi-component Ti-based filler metal

Microstructure and shear property of high-temperature brazing of TiAl alloy and 316L stainless steel with a Ni-based amorphous filler

Interfacial Microstructure and Mechanical Properties of TZM Alloy Joints Brazed Using Ti-28Ni Filler Metal

Microstructural characterization and mechanical properties of ZTA/ZTA joint brazed by Ni50Ti50 filler metal

Effect of Brazing Temperature on Microstructure and Mechanical Properties of TiAl/ZrB2 Joint Brazed with CuTiZrNi Filler

Microstructure and mechanical properties of TC4 joints brazed with Ti–Zr–Cu–Sn amorphous filler alloy

Interface structure and shear strength of brazed joints of TiAl-based alloy to middle-carbon steel