In Situ Detection of Damage in the SiC_f/Ti6242 Composite During the Thermomechanical Fatigue Test

Kong Xu,Wang Yumin,Yang Qing,Bian Fang,Zhang Xu,Zhang Guoxing,Yang Lina,Wu Ying,Yang Rui

2020-01-01

Rare Metal Materials and Engineering

Abstract:The damage of the SiCf/Ti6242 composite in the thermomechanical fatigue test was monitored by the acoustic emission (AE) technique and the high-resolution X-ray tomography. The thermomechanical fatigue test was conducted with a trapezoidal waveform to simulate the actual loading of the bladed ring. The applied stress range was 130 similar to 1300 MPa and the temperature range was 100 similar to 500 degrees C. The maximum stress was held for 2 min at 500 degrees C. The AE events emerged mainly in the loading stage and the dwell stage for the cycle where the AE signals of fiber fracture and matrix cracking were found. The matrix cracks of the unbroken specimen were detected by the high-resolution X-ray tomography. The necking of the tungsten filament in the broken fiber in the cracking region was also found. These results show that the damage mechanism of the specimen is dominated by a mixture of fiber fracture and matrix cracking.