Abstract:Silicon carbide (SiC) is a promising structural and cladding material for accident tolerant fuel cladding of nuclear reactor due to its excellent properties. However, when exposed to severe environments (e.g., during neutron irradiation), lattice defects are created in amounts significantly greater than normal concentrations. Then, a series of radiation damage behaviors (e.g., radiation swelling) appear. Accurate understanding of radiation damage of nuclear materials is the key to the design of new fuel cladding materials. Multi-scale computational simulations are often required to understand the physical mechanism of radiation damage. In this work, the effect of neutron irradiation on the volume swelling of cubic-SiC film with 0.3 mm was studied by using the combination of molecular dynamics (MD) and rate theory (RT). It was found that for C-vacancy (CV), C-interstitial (CI), Si-vacancy (SiV), Si-interstitial (SiI), and Si-antisite (SiC), the volume of supercell increases linearly with the increase of concentration of these defects, while the volume of supercell decreases linearly with the increase of defect concentration for C-antisite (CSi). Furthermore, according to the neutron spectrum of a certain reactor, one RT model was constructed to simulate the evolution of point defect under neutron irradiation. Then, the relationship between the volume swelling and the dose of neutrons can be obtained through the results of MD and RT. It was found that swelling typically increases logarithmically with radiation dose and saturates at relatively low doses, and that the critical dose for abrupt transition of volume is consistent with the available experimental data, which indicates that the rate theory model can effectively describe the radiation damage evolution process of SiC. This work not only presents a systematic study on the relationship between various point defect and excess volume, but also gives a good example of multi-scale modelling through coupling the results of binary collision, MD and RT methods, etc., regardless of the multi-scale modelling only focus on the evolution of primary point defects.

In situ high-temperature 3D imaging of the damage evolution in a SiC nuclear-fuel cladding material

In situ X-ray computed micro-tomography imaging of failure processes in Cr-coated Zircaloy nuclear fuel cladding materials

Hermeticity of SiC/SiC composite and monolithic SiC tubes irradiated under radial high-heat flux

Advanced Analytics on 3D X-ray Tomography of Irradiated Silicon Carbide Claddings

Characterization of damage mechanisms in CVI-SiC/SiC composite tubes by X-ray tomography

Analysis of Multi-scale Failure Behavior of SiC f /SiC Composite Clad Tube under Flexible Clamping Damage

Modeling of the damage and fracture behaviors of a SiC triplex tube during the burst test with elastomeric insert

Study on frictional behavior of SiCf/SiC composite clad tube clamping condition under nuclear irradiation

Primary Radiation Damage in 3C-Sic under Strain Field Studied with Molecular Dynamics Simulation

Thermomechanical Assessment of Fuel Rod Cladding Made of Zirconium Alloy and Silicon Carbide Material During Reactivity-Initiated Accident

A Multi-Scale Simulation Study of Irradiation Swelling of Silicon Carbide

Multiscale Modeling of SiCf/SiC Nuclear Fuel Cladding Based on FE-Simulation of Braiding Process

Fracture behavior of SiC f /SiC cladding with prefabricated cracks on the inner/outer wall

Hoop tensile properties and crack propagation investigation of 2D braided SiC f /SiC composite tubes: Experiments and simulations

In-situ microstructure observation of oxidized SiC layer in surrogate TRISO fuel particles under krypton ion irradiation

In-situ study on the tensile property and fracture behavior of Cr coating for nuclear fuel cladding

In situ tomographic study of a 3D-woven SiC/SiC composite part subjected to severe thermo-mechanical loads

Multi-scale Progressive Damage and Failure Behavior Analysis of Three-Dimensional Winding SiC Fiber-Reinforced SiC Matrix Composite Tube

Failure Evaluation of a SiC/SiC Ceramic Matrix Composite During In-Situ Loading Using Micro X-ray Computed Tomography

Characterization of microstructure and hardening of SiC ceramic brazed joint using TiZrCuNi filler irradiated by He ions

High Temperature Fatigue Assessment of a SiCf/SiC Ceramic Matrix Composite Using Advanced Monitoring Techniques