Abstract:The intricate spatial fiber winding structure of SiC f /SiC ceramic matrix composite (CMC) cladding tubes makes it difficult to investigate in depth the inherent evolutionary mechanism of damage failure under specific operating conditions. Therefore, in this study, based on X-ray computed tomography (X-CT) reconstruction and cross scale numerical simulation methods, combined with clamping failure experiments under specific conditions for the cladding tubes, we conduct an in-depth analysis of the material's damage, failure, and mechanical behavior in different clamped regions. The research indicates that variations in the clamped regions have a minimal impact on the overall mechanical feedback of the material, and the maximum clamping load remains essentially around 500 N. The tube damage exhibits a unique " regional progressive damage evolution mechanism," where stress differentials of 108.49% to 115.33% appear between the inner and outer surfaces in different regions, leading to variations in the initiation and propagation of cracks within these areas. Furthermore, based on the minimum potential energy principle and semi-geodesic line theory, the intricate macroscopic tube structure formed by the spatial stacking and winding of SiC f /SiC cladding tube fibers is accurately reconstructed, which is combined with macroscale and microscale local feature models to capture the fibre/matrix morphology of the material with dynamic mechanical feedbacks, and experimentally validated in this work. The results indicate that the numerical model can effectively characterize the complex mechanical damage morphology and progressive failure lows of SiC f /SiC CMC at multiscale. Simultaneously, it is observed that stress concentrations in the fiber crossover region result in a load-bearing capacity 112% to 283% higher than in other areas. This phenomenon often leads to the first occurrence of failure in this region after clamping overload, exhibiting more pronounced damage characteristics.

Fracture behavior of SiC f /SiC cladding with prefabricated cracks on the inner/outer wall

Analysis of Initial Cracking of an Interface between a Bundled Lipped Channel-Concrete Composite Wall and an Infill Wall

Modeling of the damage and fracture behaviors of a SiC triplex tube during the burst test with elastomeric insert

Analysis of Multi-scale Failure Behavior of SiC f /SiC Composite Clad Tube under Flexible Clamping Damage

Fracture Behaviour of SiCp/Al Composites with Network Architecture

In situ high-temperature 3D imaging of the damage evolution in a SiC nuclear-fuel cladding material

Damage Evolution and Fracture Behavior of C/SiC Minicomposites with Different Interphases under Uniaxial Tensile Load

Investigation on crack propagation of SiCf/SiC composite via PF-CZM method

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Strengthening and Fracture Behaviors in SiCp/Al Composites with Network Particle Distribution Architecture

Effect of Bricks-and-Mortar Architecture on Fracture Behavior of SiCp/Al Composite: A Finite Element Analysis

Multi-scale Progressive Damage and Failure Behavior Analysis of Three-Dimensional Winding SiC Fiber-Reinforced SiC Matrix Composite Tube

In-situ study on the tensile property and fracture behavior of Cr coating for nuclear fuel cladding

Interface structure and tensile failure behaviour of novel SiC f /Ti–Ti 2 AlNb hybrid laminated composite material

Multiscale Failure Mechanism Analysis of SiC Fiber-Reinforced TC17 Composite Subjected to Transverse Tensile Loading at Elevated Temperature

Multiscale Modeling of SiCf/SiC Nuclear Fuel Cladding Based on FE-Simulation of Braiding Process

Hoop tensile properties and crack propagation investigation of 2D braided SiC f /SiC composite tubes: Experiments and simulations

Study on Behavior of Dynamic Fracture in SiC Nanoparticles Reinforced Magnesium Matrix Composites

On understanding the mechanical properties and damage behavior of C f /SiC composites by indentation method

Study on frictional behavior of SiCf/SiC composite clad tube clamping condition under nuclear irradiation

Study on the fracture behavior and toughening mechanism of Si3N4/SiC(n)/SiC(w) nanocomposites