Research on damage evolution mechanisms under compressive and tensile tests of plain weave SiC f /SiC composites using in situ X-ray CT

Jiangxing Wu,Hanhuan Wang,Yantao Gao,Lijuan Sun

DOI: https://doi.org/10.1515/secm-2022-0233

IF: 1.901

2024-01-01

Science and Engineering of Composite Materials

Abstract:Abstract To investigate the damage evolution and failure mechanisms of fiber-reinforced composite materials under complex conditions, this study conducted in situ X-ray computed tomography (CT) compression and tensile tests on plain weave two-dimensional woven SiC/SiC composite materials. The obtained CT in situ image data captured the behavior of materials during loading and after failure. Using the image reconstruction of CT data, the actual microstructure and damage evolution of the material under six consecutive loading levels were accurately revealed. Three-dimensional visualization models of the composite material were established using image processing software to analyze the damage evolution under compression and tension, and the failure mechanisms were compared. The results showed that the compression and tension failure mechanisms of SiC/SiC composite materials were similar, with the transverse cracking of the matrix being the first mode of damage, followed by delamination between layers and longitudinal matrix cracking of fiber bundles. Specifically, in terms of compression failure, the strength of the fiber bundle itself has a greater influence, and fiber fracture is the main cause of ultimate material failure. On the other hand, the primary cause of tensile failure is the presence of porosity defects generated during material fabrication. Consequently, the tensile material fails earlier and can withstand lower loads.

materials science, composites

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the damage evolution and failure mechanisms of fiber - reinforced composites under complex conditions. Specifically, the research conducts compression and tensile tests on two - dimensional plain - woven SiC/SiC composites through in - situ X - ray computed tomography (CT) to capture the behavior of the material during loading and its state after failure. The research aims to accurately reveal the actual microstructure and damage evolution process of the material at six consecutive loading levels through image reconstruction of CT data, and analyze the damage evolution of the material under compression and tension through a three - dimensional visualization model, and compare its failure mechanisms. The study found that the failure mechanisms of SiC/SiC composites under compression and tension conditions are similar. Firstly, there are transverse cracks in the matrix, followed by inter - laminar delamination and longitudinal matrix cracks in fiber bundles. In particular, in terms of compression failure, the strength of the fiber bundles themselves has a greater influence, and fiber breakage is the main cause of the final material failure; while in terms of tensile failure, the pore defects generated during the material preparation process are the main cause, resulting in earlier material failure and lower load - bearing capacity.

Research on damage evolution mechanisms under compressive and tensile tests of plain weave SiC f /SiC composites using in situ X-ray CT

Characterisation of damage evolution in plain weave SiC/SiC composites using in situ X-ray micro-computed tomography

Stress Field and Damage Evolution in C/SiC Woven Composites: Image-Based Finite Element Analysis and in Situ X-Ray Computed Tomography Tests

In Situ Tensile Damage Characterization of C/C Composites Through X-ray Computed Tomography and Digital Volume Correlation

DAMAGE EVOLUTION AND MICROSTRUCTURAL CHARACTERIZATION OF A CROSS-WOVEN C/SiC COMPOSITE UNDER TENSILE LOADING

Internal Damage Evolution Investigation of C/SiC Composites Using In-Situ Tensile X-ray Computed Tomography Testing and Digital Volume Correlation at 1000 °C

In-situ Study on Compressive Behaviors of Different Types of 3D SiC/SiC Composites Using X-ray Computed Tomography and Digital Image Correlation

In-situ Characterization on Crack Propagation Behavior of SiCf/SiC Composites During Monotonic Tensile Loading

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

In Situ Experimental Investigation on the Out-Plane Damage Evolution of 3D Woven Carbon-Fiber Reinforced Composites

Tensile Damage Evolution and Mechanical Behaviour of SiCf/SiC Mini-Composites Through 4D In-Situ Micro-Ct and Data-Driven Modelling

Experimental investigation on shear damage evolution of 3D woven composites using in situ computed tomography and multi-scale digital image correlation

Experimental Investigation on Interlaminar and In-Plane Shear Damage Evolution of 2D C/SiC Composites Using Acoustic Emission and X-ray Computed Microtomography

A Quantitative Representation of Damage and Failure Response of 3D Textile SiC/SiC Ceramics Matrix Composites Subjected to Flexural Loading

Uniaxial Macro‐Mechanical Property and Failure Analysis of a 2D‐Woven SiC/SiC Composite

In situ investigation of failure in 3D braided SiCf/SiC composites under flexural loading

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

EXPERIMENTAL INVESTIGATION ON PLAIN WOVEN C/SiC COMPOSITES UNDER COMPLEX STRESS STATES

3D Characterizations of Pores and Damages in C/SiC Composites by Using X-Ray Computed Tomography

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Tensile Behaviour and Damage Evolution of A C/Sic Minicomposite Fabricated by Chemical Vapour Infiltration