Abstract:Carbon fibre reinforced silicon carbide (C/SiC) ceramic matrix composites have attracted considerable attention due to their exceptional properties and extensive potential applications as high-temperature structural materials. However, due to their complex structure and manufacturing defects, C/SiC composites exhibit intricate mechanical behaviour under thermal-mechanical-oxidative coupling environments. To date, systematic studies on the internal damage evolution and failure mechanisms of C/SiC composites under high-temperature oxidative environments are lacking. In this study, a combination of synchrotron X-ray micro-computed tomography (SR mu CT) and in-situ experiments under thermal-mechanical-oxidative coupling environments at room temperature and 1650 degrees C in air was used to characterize the internal microstructures and damage evolution processes of C/SiC composites at different loading levels. Additionally, the 3D strain fields during in-situ loading were quantitatively analysed using the Digital Volume Correlation (DVC) method. The findings underscore the substantial impact of oxidative damage on the mechanical response of C/SiC composites, particularly concerning tensile properties and fracture modes. At room temperature, severe delamination, fibre bundle pull-out and interfacial debonding occurred internally. Whereas, under high-temperature atmospheric conditions, severe fibre oxidation reactions occurred at the specimen edges, resulting in rapid porosity escalation. Crack initiation from surface defects followed by rapid inward propagation is observed. Moreover, while the strain distribution remains relatively uniform until fracture, a pronounced concentration of strain is evident near the fracture zones at room temperature, with an even greater concentration observed at 1650 degrees C. Notably, the region of concentrated strain within the 3D deformation field corresponds closely to the final fracture location, as revealed by quantitative DVC analysis.

In-situ Characterization on Crack Propagation Behavior of SiCf/SiC Composites During Monotonic Tensile Loading

In Situ X-Ray Tomography Characterisation Of 3d Deformation Of C/C-Sic Composites Loaded Under Tension

Research on damage evolution mechanisms under compressive and tensile tests of plain weave SiC f /SiC composites using in situ X-ray CT

Characterisation of damage evolution in plain weave SiC/SiC composites using in situ X-ray micro-computed tomography

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Microstructure characterization and tensile behavior of 2.5D C/SiC composites fabricated by chemical vapor infiltration

SEM in Situ Study on the Mechanical Behaviour of SiCf/Ti Composite Subjected to Axial Tensile Load

Stress Field and Damage Evolution in C/SiC Woven Composites: Image-Based Finite Element Analysis and in Situ X-Ray Computed Tomography Tests

In situ investigation of failure in 3D braided SiCf/SiC composites under flexural loading

Failure Evaluation of a SiC/SiC Ceramic Matrix Composite During In-Situ Loading Using Micro X-ray Computed Tomography

3D Characterizations of Pores and Damages in C/SiC Composites by Using X-Ray Computed Tomography

In situ transmission electron microscopy observation of the initiation and growth of microcracks in an SiC whiskerAl composite

In-situ Study on Compressive Behaviors of Different Types of 3D SiC/SiC Composites Using X-ray Computed Tomography and Digital Image Correlation

Matrix Cracking of 2D SiC/SiC Composite Characterized by in Situ SEM and Nano-Ct

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

Uniaxial Macro‐Mechanical Property and Failure Analysis of a 2D‐Woven SiC/SiC Composite

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Mechanical properties and in situ crack growth observation of SiC/SiC composites

Internal Damage Evolution of C/SiC Composites in Air at 1650 °C Studied by In-Situ Synchrotron X-ray Imaging

In-plane Mechanical Behavior and Failure Mode of a 2D-Sic/sic Composite under Uniaxial Dynamic Compression