Abstract:Microstructural evolution of a refractory tantalum-tungsten alloy（Ta-4% W） after cold rolling from small to large von-Mises strains（0.12–2.7） was quantitatively studied using transmission electron microscopy.Grain subdivision was observed to take place at two levels. Geometrically necessary boundaries nearly paralleling to slip planes enclosed volumes further divided by diffuse cells and by remnants of Taylor lattices. With increasing strain, the diffuse cells evolved into clear incidental dislocation boundaries enclosing cells, while the Taylor lattices disappeared. Grain subdivision was thus intermediate between those observed in cell forming and in non-cell forming alloys. Meanwhile, the average misorientation angle across all boundaries increased while the average boundary spacing decreased. Distributions of the microstructural parameters at each strain level were found to exhibit universal scaling laws. The microstructural evolution was found closely linking to the observed high strength and strain hardening of this alloy. Based on measured microstructural parameters, the flow stress was calculated utilizing linearly addition of the strengthening by solutes, incidental dislocation boundaries（Taylor strengthening）and geometrically necessary boundaries（Hall-Petch equation）. The relative contribution of each strength mechanism evolved with increasing strain and with microstructural evolution: solutes and friction stress dominated at small strains while boundaries dominated at larger strains. Calculated strengths were in close agreement with experimental tension tests and demonstrated an unexpectedly high and continuous parabolic hardening without transition across this large strain range.

The Evolution of Dislocation Microstructure in Electron Beam Melted Ta-2.5W Alloy During Cold Rolling

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Microstructural Evolution of Ta-4%W During Cold Rolling

Orientation Dependence of the Deformation Microstructure of Ta-4% W after Cold-Rolling

Microstructural and texture evolution investigation of laser melting deposited TA15 alloy at 500?C using in-situ EBSD tensile test

Microstructure and Strength of a Tantalum-Tungsten Alloy after Cold Rolling from Small to Large Strains

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

Analysis on hot deformation behavior and microstructural evolution of TA10 alloy smelted with the electron beam furnace

Evolutions of Grain Orientation and Dislocation Boundary in Aa1050 Aluminum Alloy During Cold Rolling from Low to Medium Strains

Microstructure evolution and recrystallization of Ti6246 alloy in hot‐rolling and annealing processes

MICROSTRUCTURAL EVOLUTION OF COLUMNAR GRAIN Al DURING COLD ROLLING II. Mircoscopic Subdivision

Texture Evolution, Microstructure, and Superelastic Properties of Different Cold-Rolled Ti-Zr-Nb-Sn Strain Glass Alloys

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

Study on High-Temperature Flow Behavior and Substructure and Texture Evolution of TA15 Titanium Alloy

Microstructure Evolution and Globularization Mechanism of Lamellar Phases in Ti6.5Al2Zr1Mo1V Produced by Electron Beam Melting

Microstructure Evolution and Mechanical Properties of a Hot-Rolled Ti Alloy

Microstructure and Mechanical Properties Evolution in HfNbTaTiZr Refractory High‐Entropy Alloy During Cold Rolling

Microstructural Evolution of IF-steel During Cold Rolling

Deformation substructural evolution in transformation-induced plasticity high-entropy alloy during cold rolling

Dislocation Evolution During Additive Manufacturing of Tungsten

Hot Pack Rolling Nearly Lamellar Ti-44Al-8Nb-(W, B, Y) Alloy with Different Rolling Reductions: Lamellar Colonies Evolution and Tensile Properties