Microstructure evolution and recrystallization of Ti6246 alloy in hot‐rolling and annealing processes

Bing Lu,Jiayu Xue,Cuntie Fan,Feng Li,Jie Ding,Hui Chang

DOI: https://doi.org/10.1002/adem.202300939

IF: 3.6

2023-08-21

Advanced Engineering Materials

Abstract:In this study, the Ti‐6Al‐2Sn‐4Zr‐6Mo (Ti6246) casted alloy was treated with two different hot rolling processes (3‐pass and 5‐pass), and the as‐rolled alloy was subsequently annealed at different temperatures (780 and 850 °C). During hot rolling, obvious changes in the morphology and microstructure of the Ti6246 alloy occurred. A large number of dislocations were generated in the rolling process, and their movement plays an important role in the microstructure evolution of the alloy. The 3‐pass hot rolling resulted in smaller grain size (0.43 μm) than that of the 5‐pass rolled sample (0.68 μm), which could be attributed to the larger deformation degree of the single pass in the 3‐pass rolling process. However, the larger deformation of the 3‐pass rolling led to higher dislocation density (34.29% of LM above 1) and more microstructure defects in the Ti6246 alloy, which further resulted in easier initiation of the prismatic and pyramidal slips of the alloy. The 5‐pass procedure can provide more deformation passes to promote the DRX of the Ti6246 alloy and the fraction of DRX can reach 33.27%. On the other hand, with the increase in the annealing temperature, the degree of recrystallization increased and the number of microstructure defects decreased. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary