Microstructure, formation mechanism and properties of plasma-sprayed Cr7C3—CrSi2—Al2O3 coatings
Yu-duo MA,Pei-wen RU,Peng-yue GAO,Yan-wei WANG,Yu-hang CUI,Wen-wei SUN,Xing-yu WANG,Lei WANG,Yong YANG,Liang WANG
DOI: https://doi.org/10.1016/s1003-6326(22)66045-x
IF: 3.752
2022-11-01
Transactions of Nonferrous Metals Society of China
Abstract:The Cr7C3—CrSi2—Al2O3 composite coatings were prepared by plasma spraying Cr7C3—CrSi2—Al2O3 and Al—Cr2O3—SiC composite powders, respectively. The microstructure, formation mechanism and properties of the two Cr7C3—CrSi2—Al2O3 composite coatings obtained by plasma spraying were investigated, and the reaction mechanism of the Al—Cr2O3—SiC system was explored. The results show that the coating obtained by plasma spraying Al—Cr2O3—SiC composite powders had thinner lamella and more tortuous interlayer interface, and the in-situ synthesized Cr7C3, CrSi2 and Al2O3 in the coating were all nano-crystallines. Compared with the Cr7C3—CrSi2—Al2O3 coating prepared by plasma spraying Cr7C3—CrSi2—Al2O3 composite powders, the plasma-sprayed Cr7C3—CrSi2—Al2O3 coating obtained from Al—Cr2O3—SiC composite powders had higher density, higher microhardness (increased by 20%), better fracture toughness and lower wear rate (reduced by 28%).
metallurgy & metallurgical engineering